gelcasting凝胶浇注
1.The forming processes of gelcasting,the microstructure of green bodies and the properties of zirconia ceramics were studied.主要研究了氧化锆陶瓷的凝胶浇注成型工艺,以及坯体的微观结构和烧成后陶瓷的力学性能,并讨论获得高性能的原因。
2.2)O_(2-y),TSDC)powders doped with 0～15% mol percents of TiO_2 were prepared by the gelcasting process.通过凝胶浇注法制备了 TiO_2掺杂量为0～15% (摩尔分数)的 TiO_2-Ce_(0。
3)gel-casting凝胶浇注法
1.Sm and Gd co-doped CeO2 (SGC) powders were prepared by the gel-casting method.通过凝胶浇注法制备了Sm,Gd共同掺杂的CeO2(SGC)粉末,将制得的粉末经1400℃高温烧结4h得到相应的SGC电解质烧结体,并对SGC粉末及相应的烧结体的性能进行了表征。
2.9(TiO2-SDC) powder was prepared from the corresponding nitrates and oxides by a gel-casting method.以硝酸盐和氧化物为原料,通过凝胶浇注法制得了摩尔分数为10%TiO2-Ce0。
3.5xSmxTiO3 powders were prepared by gel-casting process.采用凝胶浇注法制得了Sr1-1。
4)gel-casting凝胶浇注成型
5)gelcasting凝胶浇注成型
1.Concentrated SiC slurry with Y2O3 and Al2O3 as sintering assistants was prepared, by using the medium of gelcasting premix solution and pH adjusting reagent of TMAH (tetramethylammonium hydroxide).采用一种凝胶浇注成型预配液作为陶瓷粉体的分散介质,将亚微米级SiC粉体和烧结助剂Y2O3、Al2O3直接混合,制得了固含量>50vol％的凝胶浇注浆料,在100s-1的剪切速率下,浆料粘度<1Pa·s,可以顺利实现凝胶浇注成型;对得到的SiC素坯进行了无压烧结。
2.Water soluble epoxy resin was used as gel former in the zirconia gelcasting process.研究了氧化锆凝胶浇注成型工艺中,水溶性环氧树脂凝胶剂对浆料的流变性和固化过程的影响。
6)gelcasting凝胶浇注成形
1.Preparing and gelcasting of high concentrated titanium carbide suspension;高固相含量碳化钛悬浮体的制备和凝胶浇注成形