聚酰胺酰亚胺,polyamide-imide英语短句,例句大全

聚酰胺酰亚胺,polyamide-imide
1)polyamide-imide聚酰胺酰亚胺
1.Preparation and application of polyamide-imide;聚酰胺酰亚胺的制备及其应用
2.Polyamide acid was synthesized by polycondensation of trimellitic anhydride chloride(TMAC) and 4,4′-diaminodiphenylether(DDE) in N,N-dimethylacetamide(DMAC),and then coverted into polyamide-imide by treating with acetic anhydride and triethlamine mixture.以合成的高纯度偏苯三酸酐酰氯(TMAC)和4,4′-二氨基二苯醚为原料,N,N-二甲基乙酰胺为溶剂,制备聚酰胺酸预聚体,再用醋酐和三乙胺将其亚胺化得到聚酰胺酰亚胺(PAI),考察了聚合反应条件对分子量的影响,用FT-IR1、H-NMR表征了PAI的结构,并采用热失重(TGA)和差动扫描量热分析仪(DSC)对PAI进行热性能研究。
3.Heat-resistant self-bonding polyamide-imide varnish for magnet wire is formulated with trimellitic anhydride and diisocyanate as raw materials, N-methylpyrrilidone as solvent by controlling reaction temperature, reaction time, reaction progress and polymerization degree, and adding different additive agents.以偏苯三酸酐和二苯基甲烷二异氰酸酯为原料,N-甲基吡咯烷酮为溶剂,控制反应温度、时间、反应进程、聚合度,适时添加各种助剂,制备性能优良的耐高温聚酰胺酰亚胺自粘电磁线漆。
2)Polyamide imide聚酰胺酰亚胺
1.A polyamide imide was synthesized from trimelltic anhydride and di isocyanate.本文用偏苯三酸酐和二异氰酸酯合成了一种新型聚酰胺酰亚胺。
3)poly(amide-imide)聚酰胺酰亚胺
1.A series of poly(amide-imide)s(PAIs) were prepared from the diacid and various aromatic diamines via Yamazaki-Higashi reaction in N-methyl-2pyrrolidone,with triphenyl phosphite and pyridine as condensing agents,and calcium chloride as catalyst.以此两种酸为原料、N-甲基-2-吡咯烷酮(NMP)为溶剂、亚磷酸三苯酯(TPP)与吡啶为缩合剂、氯化钙为催化剂,通过Yamazaki-Higashi反应,直接与3种芳香族二胺单体反应制得一系列聚酰胺酰亚胺(PAI)。
4)Polyimide[英][,p?li'imaid][美][,pɑli'?m,a?d]聚酰亚胺
1.Synthesis and properties of sulfonyl-substituted polyimides with high refractive indices and high transparency;砜基取代高折射率高透明性聚酰亚胺的合成与性能
2.Study on polyimide resin modified by nano-Si_3N_4 for diamond tools;金刚石磨具纳米Si_3N_4改性聚酰亚胺树脂结合剂研究
3.Effect of coupling agent on microstructure and properties of polyimide/SiO_2 hybrid membrane;偶联剂对聚酰亚胺/SiO_2杂化膜性能的影响

英文短句/例句

1.Preparation of carbon membranes from poly(urethane imide) and poly-imide copolymers聚氨酯酰亚胺-聚酰亚胺嵌段共聚物制备炭膜
2.STUDY ON STORE-STABILITY OF POLY(AMIC ACID)S AND HYPERBRANCHED POLYIMIDE聚酰胺酸稳定性和超支化聚酰亚胺的研究
3.Preparation and Study of Polyimide and Poly (Amic Acid) Micro-and Nano-spheres聚酰亚胺及聚酰胺酸微纳米颗粒的制备及研究
4.Synthesis of pyridine-containing copolyimide via chemical imidization method化学亚胺化合成含吡啶环共聚聚酰亚胺
5.Polyimide is a macromolecule polymer material.聚酰亚胺是一种高分子聚合物材料。
6.Study on modification of PMDA/ODA-copolyimidePMDA/ODA型聚酰亚胺的共聚改性研究
7.Synthesis and Characterization of Organic Soluble Polyisoimides and Polyimides;有机可溶性聚异酰亚胺及聚酰亚胺的合成与性能研究
8.Preparation of Polyaniline/Polyamide/Polyaniline Compound Films by In-Situ Deposition原位聚合沉积制备聚苯胺/聚酰亚胺/聚苯胺复合膜
9.Preparation of polyimide nanoparticles by imidization and re-precipitation两步亚胺化-再沉淀法制备聚酰亚胺纳米粒子
10.Preparation and Application of Chemical Imidizied Polyimides化学亚胺化聚酰亚胺的制备及其应用研究
11.Study on Preparing Polyimide Fibers via Partly Imidized Process of Poly(Amic Acid);聚酰胺酸部分成环合成法制备聚酰亚胺纤维的研究
12.Study on Preparing Polyimide Regular Fiber and Nanofiber via Partly Imidized Process of Poly(Amic Acid);聚酰胺酸部分成环法制备聚酰亚胺湿纺纤维和电纺纤维的研究
13.polyimide woven glass fabric copper-clad laminates聚酰亚胺玻璃布覆铜箔板
14.The Dielectric Characteristic Research of Nano-Composite Polyimide Film;纳米复合聚酰亚胺薄膜的介电性研究
15.Preparation and Characterization of Polyimide/SiO_2-TiO_2 Hybrid Film;聚酰亚胺/SiO_2-TiO_2杂化薄膜的制备与表征
16.The Research of Capacitive Humidity-sensitive Properties of FLUPI;改性聚酰亚胺电容式湿敏材料的研究
17.Synthesis and Studies of New Photosensitive Polyimides;新型感光聚酰亚胺的合成和性能研究
18.Study of Inorganic Nano-Particles/Polyimide Hybrid Film;无机纳米/聚酰亚胺杂化薄膜的研制

相关短句/例句

Polyamide imide聚酰胺酰亚胺
1.A polyamide imide was synthesized from trimelltic anhydride and di isocyanate.本文用偏苯三酸酐和二异氰酸酯合成了一种新型聚酰胺酰亚胺。
3)poly(amide-imide)聚酰胺酰亚胺
1.A series of poly(amide-imide)s(PAIs) were prepared from the diacid and various aromatic diamines via Yamazaki-Higashi reaction in N-methyl-2pyrrolidone,with triphenyl phosphite and pyridine as condensing agents,and calcium chloride as catalyst.以此两种酸为原料、N-甲基-2-吡咯烷酮(NMP)为溶剂、亚磷酸三苯酯(TPP)与吡啶为缩合剂、氯化钙为催化剂,通过Yamazaki-Higashi反应,直接与3种芳香族二胺单体反应制得一系列聚酰胺酰亚胺(PAI)。
4)Polyimide[英][,p?li'imaid][美][,pɑli'?m,a?d]聚酰亚胺
1.Synthesis and properties of sulfonyl-substituted polyimides with high refractive indices and high transparency;砜基取代高折射率高透明性聚酰亚胺的合成与性能
2.Study on polyimide resin modified by nano-Si_3N_4 for diamond tools;金刚石磨具纳米Si_3N_4改性聚酰亚胺树脂结合剂研究
3.Effect of coupling agent on microstructure and properties of polyimide/SiO_2 hybrid membrane;偶联剂对聚酰亚胺/SiO_2杂化膜性能的影响
5)PI[英][pai][美][pa?]聚酰亚胺
1.Stability of Nanoparticles in PI-Inorganic Hybrid Films;无机纳米杂化聚酰亚胺薄膜纳米颗粒特性研究
2.Development of advanced composite materials PI;聚酰亚胺先进复合材料的研究进展
3.The Experiment of Observing PI Damage Causing by Static Electricity;液晶盒中聚酰亚胺静电击伤的观测实验
6)Polyimide(PI)聚酰亚胺
1.Polyimide(PI) film etched by electron beam(EB) to produce PI micron-hole separation membrane combined with the methods of masks and oxygenation corrosion was studied in this paper.以电子束蚀刻技术,结合微孔掩膜和溶液氧化腐蚀的方法,制备聚酰亚胺(Polyimide,PI)微孔分离膜。
2.Using TG-DTG,DSC and IR techniques,the non-isothermal decomposition kinetics of a new polyimide(PI) which is synthesized by 3,3′,4,4′-benzophenone tetracarboxylic dianhydride(BTDA) and 4,4′-(1,3-phenylenedioxy)-dianiline(CAS: 2479-461),were studied.通过热重法、差示量热扫描法以及红外光谱法研究了由3,3,′4,4-′benzophenone tetracarboxy licd ianhydride(二苯酮四酸二酐,简称BTDA)和4,4-(′1,3-pheny lened ioxy)-d ian iline(CA S:2479-461)所形成的一种新型聚酰亚胺的非等温热分解过程,测得其失重5%温度为492℃,失重10%温度为530℃。
3.As a kind of polymer material, polyimide(PI) holds a favorable complanation property and is easy to become ash in the oxygen.聚酰亚胺树脂(PI)因其良好的平面化特性、在氧气中易灰化、不完全固化易溶解于碱性显影液、在CHF3等离子气氛中有较强的抗蚀性等性质,在电容RFMEMS开关的制作过程中,应用它作为刻蚀保护层和牺牲层,不但可以使工艺过程得到简化,而且可以对开关的介质层尺寸、牺牲层厚度等图形参数起到很好的控制作用。