多孔薄膜,porous films英语短句,例句大全

多孔薄膜,porous films
1)porous films多孔薄膜
1.Nanocrystalline titania porous films were prepared on glass substrates with Ti(OC4 H9)4 as precursor and polyethy-lene glycol (PEG) as organic template by sol - gel process.采用溶胶-凝胶技术,以钛酸丁酯[Ti(OC_4H_9)_4]为前驱体,加入聚乙二醇(polyethylene glycol,PEG)作为模板剂,在玻璃基片上制备了纳米氧化钛多孔薄膜。
2.The forming mechanism of colloid crystal was discussed; the advantage of dip-drawing method to assemble PS template and fill SnO2 sol was exhibited; the influence of fabricating parameters on the array quality, the number of spheres and morphology of porous films was studied; and the structure and optical properties of PS.本文采用浸渍-提拉法组装了PS胶体晶阵列,并以此为模板制备了SnO2有序多孔薄膜。
3.Highly-ordered Nanocrystalline ZnO porous films with high thermal stability were synthesized using zinc acetate (Zn(CH_3COO)_2·2H_2O) as precursor and organic surfactant (polyethylene glycol (PEG), polystyrene spheres (PS)) as templates.本实验以醋酸锌(Zn(CH_3COO)_2·2H_2O)为原料,以高分子表面活性剂(聚乙二醇PEG和聚苯乙烯微球PS)为模板,合成了热稳定性较好的ZnO多孔薄膜。

英文短句/例句

1.The Preparation and Characterization of TiO_2 Thin Films and Porous TiO_2 Thin Films by Sol-Gel MethodTiO_2薄膜及其多孔薄膜的溶胶—凝胶法制备与表征
2.Studies on Nano-crystalline ZnO Porous Films Prepared by Wet-chemical Method;纳米ZnO多孔薄膜的湿化学法制备研究
3.Studies on the Templating Preparation of ZnO Porous Films;ZnO多孔薄膜的模板组装制备研究
4.Studies on the Templating Preparation of Nanocrystalline TiO_2 Porous Films;纳米TiO_2多孔薄膜的模板组装制备研究
5.Morphology of Porous Pt Films Formed on Ti Substrate with Template Method模板制备钛基铂多孔薄膜的形貌观察
6.Synthesis of Porous TiO_2 Films by Anodic Oxidation阳极氧化法制备TiO_2多孔薄膜
7.Templating Assembly of ZnO Ordered Porous Films and Their Electrode Performance;ZnO有序多孔薄膜的模板组装及电极性能
8.Surface Modification of TiO_2 Nanoporous Film and Its Photoelectrochemical Properties;TiO_2多孔薄膜的表面修饰及其光电化学性能
9.Studies of Nanoporous TiO_2 Photoelectrodes of Dye-sensitized Solar Cells;染料敏化太阳能电池TiO_2多孔薄膜电极研究
10.Preparation and Chacterization of Eosin Y Sensitized TiO_2 Nanoporous Film Dye-Sensitized Solar Cells;曙红敏化纳米晶TiO_2多孔薄膜太阳能电池的研究
11.Studies on Ordered Structure of Porous Nanocrystalline TiO_2 Films Prepared by Sol-Gel Process;溶胶—凝胶纳米TiO_2多孔薄膜的结构有序化研究
12.Preparation and Study of Porous TiO_2-SiO_2 Composite Thin Films;多孔SiO_2-TiO_2复合薄膜的制备及研究
13.Novel Method of Fabricating Porous Silica Film with Two Step Catalyze Sol-Gel Process溶胶凝胶法制备多孔SiO_2薄膜的新方法
14.Investigation of Nano-SiC Film Photoluminescence and Nanoporous SiO_2:F Film with Low Dielectric Constant;纳米SiC薄膜的发光与多孔SiO_2：F薄膜介电特性研究
15.Investigation of Luminescence of Organic Thin Films and Exploration for Luminescence of Porous Silicon;有机薄膜发光的研究及多孔硅发光的初步探讨
16.Electrodeposition of Porous Metal Films on a Template of Hydrogen Bubbles;氢气泡模板法电沉积制备多孔金属薄膜
17.The Effect of O Plasma Treatment on Porous SiCOH Films;多孔SiOCH薄膜的O等离子体表面处理研究
18.The Research of the Structure and Electrical Property of the Porous Low k SiO_2: F Film;多孔低k SiO_2：F薄膜的结构和电学性质研究

相关短句/例句

porous film多孔薄膜
1.Nanocrystalline titania porous films are prepared on glass substrates via a sol-gel dip-coating method from a tetrabutylorthotitanate solution that contains diethanolamine as the stabilizer of titanium alkoxide and polyethylene glycol (PEG) as a template.以钛酸丁酯为无机原料、二乙醇胺作稳定剂 ,加入聚乙二醇 (PEG)作模板制备前驱体溶胶 ,通过溶胶凝胶工艺和浸渍提拉技术在玻璃基片上制备了孔径在 10～ 10 0 0nm范围内可调的纳米TiO2 多孔薄膜。
2.ZnO porous films were prepared on glass substrates by PEG-assisted sol-gel method using Zn(CH_3COO)_2·2H_2O as precursor,ethanol as solvent and NH(C_2H_2OH)_2 as chelating agent.以醋酸锌为前驱体,乙醇为溶剂,二乙醇胺为络合剂,通过聚乙二醇(PEG)辅助的溶胶———凝胶法在玻璃基片上制备了ZnO多孔薄膜。
3.ZnO porous films were prepared on glass substrates by solgel method using polyethylene glycol (PEG2000) as organic template, Zn(CH_3COO)_2·2H_2O as precursor, ethanol as solvent and NH(C_2H_4OH)_2 as chelating agent.以聚乙二醇(polyethyleneglycol,PEG2000)为模板剂,醋酸锌(Zn(CH3COO)2·2H2O)为前驱体,乙醇为溶剂,二乙醇胺[NH(C2H4OH)2]为络合剂,通过溶胶凝胶法在玻璃基片上制备了ZnO多孔薄膜。
3)porous TiO2 thin films多孔TiO2薄膜
1.The porous TiO2 thin films deposited on the surface of common glass surface were prepared from alkoxide solutions containing polyethylene glycol (PEG) by dip-coating technique.配制了含不同分子量聚乙二醇的TiO2溶胶,采用浸渍提拉法在普通载玻片上制备了单、双层多孔TiO2薄膜。
4)porous SiCOH ultra-low-k film多孔SiCOH薄膜
5)porous silica film多孔SiO2薄膜
1.Taking ammonia,acetic acid as catalyzer,TEOS as Si sources,glycerin as anti-cracking agent,PVA1750 as ingredients and foaming agent,porous silica film was fabricated.以氨水、醋酸为催化剂,用正硅酸已酯(TEOS)为Si源,甘油作为防裂剂,聚乙烯醇(PVA1750)作为致缓剂和发泡剂,制作多孔SiO2薄膜。
6)porous β-SiC film多孔SiC薄膜