1)dechromisaion脱铬腐蚀
1.It was found that Cu of CuNiCrAl alloy in low temperature H_2SO_4 solutions is easier subject to corrosion than Cr; and dechromisation of the CuNiCrAl alloy occurs at a certain concentration and temperature of H_2SO_4 solutions,and the tendency of dechromisaion of the CuNiCrAl alloy increases with increasing concentration and temperature of H_2SO_4 solutions.结果表明:CuNiCrAl合金在低温H_2SO_4溶液中,合金中的Cu相较易腐蚀;当H_2SO_4溶液浓度和温度达到一定值时,合金出现脱铬腐蚀现象,溶液的浓度和温度越高,脱铬倾向越大,且溶液添加NaCl能促进合金的脱铬腐蚀,还对CuNiCrAl合金的脱铬机制进行了探讨。
英文短句/例句
1.EFFECT OF THE SAMPLE STATE ON DECHROMIZATION OF Cu-Cr ALLOY试样状态对Cu-Cr合金脱铬腐蚀的影响
2.Corrosion resistance of Ni-Cr and Ni-Cr-Ti alloy in artificial saliva镍铬和含钛镍铬烤瓷合金的耐腐蚀性能研究
3.Experiment on the Anti-corrosion Property of Chrome Molybdenum Steel Tube in Naphthenic Acid Environment铬钼钢管耐高温环烷酸腐蚀性能试验
4.The failure was caused by dezincification corrosion.结果表明：凝汽器铜管的腐蚀属栓状脱锌腐蚀。
5.The rough chrome plating is for mating to other chrome plated equipment and for additional corrosion resistance.未抛光镀铬表面适合其它镀铬设备，并且具有更强的防腐蚀能力。
6.The Corrosion Resistance of Ni-Cr Alloy, Ni-Cr Alloy with Titanium and Alloys after Surface Treatment;镍铬合金、含钛镍铬合金及其表面处理后材料的耐腐蚀性研究
7.Electrodeposited chromium coatings--Electrolytic corrosion testing (EC test)GB/T6466-1986电沉积铬层电解腐蚀试验(EC试验)
8.MATHEMATIC MODEL OF RELATION BETWEEN CORROSION RATE AND Si CONTENT OF Cr-Ni STAINLESS STEEL铬镍不锈钢的腐蚀率与硅含量关系的数学模型
9.For example, chromium may be included to resist corrosion and tungstem to increase hardness.例如，加铬后能耐腐蚀；加钨后可增加硬度。
10.Mechanism of corrosion resistance for alloys prepared by surface metallurgy with Cr and Ta ion beams铬、钽离子束表面冶金合金的抗腐蚀机制
11.The Electrochemical Research of Heat Treatment in the Corrosion Behavior for Dental Co-Cr Alloys;热处理对牙用钴铬合金腐蚀性能的电化学研究
12.Research on Improving the Corrosion Resistance of Porcelain-fused Nickel-chromium Alloys by Sol-gel Coating;溶胶凝胶技术提高镍铬合金耐腐蚀性的研究
13.The Contrastive Research on the Corrosion Resistance of Ni-Cr Alloy with Different Coatings;镍铬合金表面不同涂镀层抗腐蚀性能对比研究
14.Corrosion Behavior of Intraoral Fluoride Controlled-release Device to Chromium-cobalt Castings;氟化物控释装置对钴铬合金腐蚀性的实验研究
15.Influence of Candida Albicans' Adhesion on Corrosion of Ti Alloy and Co-Cr Alloy白色念珠菌对钛合金，钴铬合金腐蚀的影响
16.Corrosion Behavior of Ni-Cr PFM Alloy Fabricated by Laser Rapid Forming Technology激光快速成形镍铬烤瓷合金腐蚀性能研究
17.Corrosion behaviors of chrome steel during impact and abrasion in simulative mineral slurry铬钢在模拟矿浆中受冲击磨损时的腐蚀行为
18.Effect of copper on corrosion resistance of Cr-Mn stainless steel in Cl~- solutionCu对铬锰钢在Cl~-环境中腐蚀行为的影响
相关短句/例句
chromate corrosion铬酸腐蚀
3)dezincification[英][di:,zi?k?f?'kei??n][美][di,z??k?f?'ke??n]脱锌腐蚀
1.Effect of Bi Content on the Dezincification Property of the Brass铋含量对黄铜脱锌腐蚀性能的影响
2.The effect of cold-deformation amount and annealing temperature on the dezincification of the unleaded free-cutting brass were investigated.采用脱锌腐蚀深度测量方法,光学显微镜分析和SEM等分析方法,研究了不同的冷变形量和退火温度对无铅易切削铋黄铜的耐脱锌腐蚀性能的影响。
3.The results show that the main cause of the original corrosion leakage of H68A condenser brass copper tubes is dezincification and.结果表明,造成H 68A凝汽器黄铜管腐蚀泄漏的主要原因是脱锌腐蚀。
4)den-ickel corrosion脱镍腐蚀
5)dezincification corrosion脱锌腐蚀
1.The failure was caused by dezincification corrosion.结果表明:凝汽器铜管的腐蚀属栓状脱锌腐蚀。
2.The results show that the failure of oil-cooler is bolt-like dezincification corrosion.结果表明 ,冷油器铜管的腐蚀属于栓状脱锌腐蚀。
3.The paper presents some results obtained from a research about effects of rare-earth(RE)and boron(B)refining on the microstructure and dezincification corrosion properties of casting lead brass.研究了加入稀土和硼细化处理对铸造铅黄铜组织和脱锌腐蚀性能的影响。
6)dealuminification corrosion脱铝腐蚀
1.TEM observation on dealuminification corrosion of QAl9-2 alloy in marine environment;QAl9-2合金脱铝腐蚀的TEM研究
延伸阅读
点腐蚀和缝隙腐蚀 金属材料接触某些溶液，表面上产生点状局部腐蚀，蚀孔随时间的延续不断地加深，甚至穿孔，称为点腐蚀（点蚀），也称孔蚀。通常点蚀的蚀孔很小，直径比深度小得多。蚀孔的最大深度与平均腐蚀深度的比值称为点蚀系数。此值越大，点蚀越严重。一般蚀孔常被腐蚀产物覆盖，不易发现，因此往往由于腐蚀穿孔，造成突然性事故（见金属腐蚀）。 缝隙腐蚀是两个连接物之间的缝隙处发生的腐蚀，金属和金属间的连接（如铆接、螺栓连接）缝隙、金属和非金属间的连接缝隙，以及金属表面上的沉积物和金属表面之间构成的缝隙，都会出现这种局部腐蚀。 许多金属材料都能产生点蚀和缝隙腐蚀。不锈钢、铝合金等靠钝化来增强耐蚀性的金属材料，也易产生点蚀和缝隙腐蚀。许多环境介质都能引起金属材料的点蚀和缝隙腐蚀，尤其是含氯离子的溶液。 点腐蚀 金属表面的电化学不均匀性是导致点蚀的重要原因。金属材料的表面或钝化膜等保护层中常显露出某些缺陷或薄弱点(如夹杂物、晶界、位错等处)，这些地方容易形成点蚀核心。金属浸入含有某些活化阴离子（特别是氯离子）的溶液中，只要腐蚀电位达到或超过点蚀电位（或称击穿电位），就能产生点蚀。这是由于钝化膜在溶液中处于溶解以及可再度形成的动平衡状态,而溶液中的活化阴离子(氯离子)会破坏这种平衡,导致金属的局部表面形成微小蚀点，并发展为点蚀源。例如不锈钢表面的硫化物夹杂的溶解，暴露出钢的新鲜表面，就会形成点蚀源。 点蚀的发展是一个在闭塞区内的自催化过程。在有一定闭塞性的蚀孔内,溶解的金属离子浓度大大增加,为保持电荷平衡，氯离子不断迁入蚀孔，导致氯离子富集。高浓度的金属氯化物水解，产生氢离子，由此造成蚀孔内的强酸性环境，又会进一步加速蚀孔内金属的溶解和溶液氯离子浓度的增高和酸化。蚀孔内壁处于活化状态（构成腐蚀原电池的阳极），而蚀孔外的金属表面仍呈钝态（构成阴极），由此形成了小阳极／大阴极的活化-钝化电池体系，使点蚀急速发展。 缝隙腐蚀 是由缝隙内外介质间物质移动困难所引起的。为此，缝隙的宽度应足够狭小。它的发展也是一个闭塞区内的自催化过程。例如处在海水等介质中的钢制零部件，在缝隙腐蚀的起始阶段，缝隙内外的金属表面都发生以氧还原作为阴极反应的腐蚀过程。由于缝隙内的溶氧很快被消耗掉，而靠扩散补充又十分困难，缝隙内氧还原的阴极反应逐渐停止，缝隙内外建立了氧浓差电池。缝隙外大面积上进行的氧还原阴极反应，则促进缝隙内金属阳极溶解。缝隙内金属溶解产生过剩的金属阳离子(Me+),又使缝隙外的氯离子迁入缝隙内以保持电平衡。随之而发生的金属离子水解，使缝隙内酸度增高，又加速了金属的阳极溶解（见图)。 点腐蚀和缝隙腐蚀的比较 点腐蚀和缝隙腐蚀两者的发展阶段的机理是一致的，但是它们的诱发机理和发生过程则有所不同。前者是由于材料的钝态或保护层的局部破坏所引起,通过形成点蚀源而发展起来的;后者则是因介质的电化学不均匀性所引起，腐蚀一开始就在缝隙条件下受闭塞电池的作用。从电极电位来看，发生和发展缝隙腐蚀的电极电位比点蚀更低。从介质来看，缝隙腐蚀在不含氯离子的溶液中也会发生，而点蚀则多在含有特殊的活性阴离子条件下才会发生。 溶液中的氯离子浓度对两种腐蚀有很大的影响，通常是氯离子浓度愈高，点蚀和缝隙腐蚀发生的可能性也愈大，而且发展的速度也愈快。其他卤族离子也有类似的影响。一般溶液的温度愈高，产生点蚀和缝隙腐蚀的危险性也愈大。 防止措施 提高材料耐点蚀性的重要措施是添加适当的合金元素（如在不锈钢中添加钼），采取钝化处理及适当的热处理，降低金属材料中的夹杂物含量。防止缝隙腐蚀的主要措施是在结构中要避免缝隙和能造成表面沉积的几何形状，要尽量用焊接代替铆接，采用非吸湿性材料做垫圈。电化学保护对防止点蚀和缝隙腐蚀都有效。采用合适的耐点蚀和耐缝隙腐蚀的金属材料也是防止点蚀与缝隙腐蚀的有效措施。 参考书目 Localized Corrosion, National Association of Corrosion Engineers,Houston,Texas,1974.