补焊,repair welding英语短句,例句大全

补焊,repair welding
1)repair welding补焊
1.Microstructure analysis of activated repair welding joint of TA15 titanium alloy;TA15钛合金接头活性剂补焊的组织特征
2.The Development and Application of the Casting Defect Repair Welding Machine;铸件缺陷补焊机的研制与应用
3.Discussion on repair welding method for converter mouth;转炉炉口补焊方式的探讨

英文短句/例句

1.Ceramic Cushion of Steel Pipe Weld Aided Device and Its Welding Procedure钢管焊缝陶瓷垫补焊装置及焊接工艺
2.Study on High Efficient Bonding and Repaired Welding Process of TA15 Titanium Alloy;TA15钛合金高效焊接及补焊工艺研究
3.CO_2+O_2 Mixed GMAW Welding Gray Cast IronCO_2+O_2混合气体保护焊补焊灰铸铁
4.The Welding Experimentation of 12Cr1MoVG Tube Platen and Analysis of Manual Arc Welding Cracks膜式窄节距12Cr1MoVG管屏埋弧焊接试验及手工电弧焊补焊裂纹分析
5.Welding Process for 2A12-T4 of Aluminum Alloy铝合金2A12-T4壳体零件补焊工艺
6.5CrNiMo Die Forging Welding Technology5CrNiMo锤锻模具补焊工艺方法
7.Residual stress analysis of repair welding at different zone of Q345R welded joint based on finite element simulationQ345R钢焊接接头不同部位补焊残余应力的有限元分析
8.Analysis of the Reason of Crackles in the Course of Mend－Weld of Cast Iron and Its Preventive Measures;铸铁补焊产生裂纹原因的剖析及其防止措施
9.welded reinforcement of nozzle opening接管开孔的焊接补强
10.Study on the Welding Wire Used in Repairing ZL205A Alloy Castings;ZL205A铝合金铸件焊补用焊丝的研究
11.Analysis and Patching for Cracks which Appeared after the 2000m~3 Spherical Tank Assembling Weld2000m~3球罐组焊裂纹分析与修补
12.Real-time Interpolation Algorithm for Trajectory Planning Based on Welding Robot基于焊接机器人的实时轨迹插补算法
13.Specially suitable for zinc patching of weld seam in tube welding line, and capacitor spray.本套设备适合于高频焊管生产线上进行焊缝的补锌及电容喷涂。
14.Automatic offset function for long cable up to 100m.具有焊线长的自动补偿功能，焊接电缆可长至100米.
15.You must weld and grind this area before painting.在油漆之前你必须把这个地方电焊修补、磨好。
16.Compensating Conservation of Parallel Condenser of AC Arc Welder and Its Calculation交流弧焊机并联电容补偿节电及其计算
17.Causes and preventive measures for soledering cracks on bearing surface of adapter承载鞍支承面焊补裂纹的形成原因及防止措施
18.Study on Optimized for Welding Process of the Crack in High-pressured Cylinder of Steam Turbine汽轮机高压缸体裂纹焊补工艺优化研究

相关短句/例句

Repairing welding补焊
1.The feasibility of Ti alloy multiple repairing welding was discussed.采用光学显微镜、X射线衍射仪和电子探针等测试手段分析TA15钛合金熔焊接头补焊微观组织特征,探讨钛合金焊缝多次补焊的可行性。
2.After repairing welding treatment,the 5 treated cast steel valves in Tuoketuo Power Plant have not found any leakage after two years operation.通过对托克托发电厂的铸钢阀门进行补焊消缺处理,处理的5个阀门经运行两年多的考验,未发生泄漏。
3.It introduces clearly the repairing welding for the large inlet gate valve from the points such as welding performance analysis,welding materials selection and welding proless etc.从焊接性能分析、焊接材料选用及焊接操作工艺等方面 ,对大型进口闸阀的补焊进行了较详细的论
3)Weld[英][weld][美][w?ld]补焊
1.The new method of welding impeller crack with low alloy high intensity steel is introduced,and analyze the performance and elements of impeller after welding,the suggestion of weld impeller crack with low alloy high intensity steel is put forward.介绍了低合金高强度钢焊接叶轮裂纹补焊新方法,并对叶轮补焊后的性能和成分进行了分析,对低合金高强度钢焊接叶轮裂纹补焊提出了建议。
4)repair weld补焊
1.The chemical compositions of welds' bottom layer and other deposited welds of repair welded ZG15Cr1Mo1V castings, using EniCrFe-3 electrodes, E2-26-21-16(A402) or E0-19-10Nb-16(A512) austenite stainless steel electrodes, are evaluated separately.文章分别计算了ENiCrFe-3焊条、奥氏体不锈钢焊条E2-26-21-16(A402)和E0-19-10Nb-16(A132)补焊ZG15Cr1Mo1V后的底层焊缝和其它堆焊层焊缝的化学成分,得出选用镍基焊材(ENiCrFe-3)补焊ZG15Cr1Mo1V时,允许化学成分在较大的范围内选择,补焊金属均能获得奥氏体相的铁基合金和镍基合金。
2.A special repair weld procedure,which performed multi-pass welding on each seam and grinds the surface layer,together with preheating and post-heating process,resulted in no cracks in the weld joint any longer.介绍了脱水脱烃装置中原料气预冷器的基本情况,对其管箱/管板角焊接接头开裂后补焊又产生新裂纹的原因进行了分析,采用每层多道焊并磨去焊缝表面层、焊前预热及后热的特殊工艺进行返修后,焊接接头再未发生开裂现象。
5)repair welding焊补
1.Studies of silver-contained solder for repair welding on surfaces of steel castings;铸钢件表面焊补含银钎料的研究
2.The article introduces a repair welding technology which prevents the worn axis from residual deformation and assures the repaired axis normally running.介绍了一种防止磨损轴在焊补过程中出现残余变形,以保证修复轴正常运转的轴磨损无变形焊补工艺。
3.The heavy duty mill housing casting made of GS-20Mn5V,weighted 400t,in which the cracks were found during the casting cleaning,in this case the repair welding must be performed as well as the entire stress relieving.铸件清理时发现裂纹,必须进行焊补和焊后整体消应。
6)welding[英][weld][美][w?ld]焊补
1.The technique and experience of in situwelding repair wheels in Lai Steel were presented.本文简要分析了影响烧结风机转子使用寿命的因素 ,介绍了莱钢对 950 0风机转子进行机上焊补的技术和经验。
2.A formula between cast iron welding measure and t 8/5  is built up according to the conduction throry and the feature of welding in this paper.根据传热学理论和焊补特点，建立了铸铁焊补尺寸与ｔ８５关系式。