铜腐蚀,copper corrosion英语短句,例句大全

铜腐蚀,copper corrosion
1)copper corrosion铜腐蚀
1.The test results showed that the five factors affecting copper corrosion in a descending order as:pH, rotation speed, dissolved oxygen,: time and temperature.通过准动态正交试验(L1645),研究了时间、水温、转速、pH值、溶解氧等因素对发电机内冷水系统中铜导线腐蚀的影响,结果表明:各因素对铜腐蚀影响的顺序从大到小依次为:pH值、转速、溶解氧、试验时间、水温、当试液pH值分别为6。

英文短句/例句

1.Relationship between bronze corrosion and relative humidity in the existence of SO_2在SO_2存在下青铜腐蚀与相对湿度的关系
2.a bronze with 2-3% silicon that is resistant to corrosion.含%硅的青铜，抗腐蚀。
3.Study of Corrosion and Inhibition of Copper Clad Laminate and Reinforced Concrete;覆铜板、钢筋混凝土腐蚀与缓蚀的研究
4.The failure was caused by dezincification corrosion.结果表明：凝汽器铜管的腐蚀属栓状脱锌腐蚀。
5.Study on corrosion behavior of rare-earth aluminum brass in NaCl+NH_4Cl solution稀土铝黄铜合金在NaCl+NH_4Cl腐蚀液中的腐蚀行为
6.testing method for copper corrosion of petroleum products石油产品铜板腐蚀试验方法
7.testing method for copper corrosion of greases润滑脂类铜板腐蚀试验方法
8.Industrial aromatic hydrocarbons--Test method of copper corrosionGB/T11138-1994工业芳烃铜片腐蚀试验法
9.Copper-zinc alloys--Determination of dezincification corrosion resistanceGB/T10119-1988黄铜耐脱锌腐蚀性能的测定
10.Lubricating grease--Corrosiveness to copper--Copper strip testGB/T7326-1987润滑脂铜片腐蚀试验法
11.Petroleum products--Corrosiveness to copper--Copper strip testGB/T5096-1985石油产品铜片腐蚀试验法
12.Test for copper strip corrosion of engine fuelsGB/T378-1964发动机燃料铜片腐蚀试验法
13.Study on Surface Passivation and Resistance to Environmental Corrosion of Brass;黄铜表面钝化处理与耐环境腐蚀研究
14.Anticorrosive Study of Self-assemble Monolayers of 1-dodecanethiol on Copper;铜表面十二硫醇膜的抗氧化腐蚀研究
15.Erossion-Corrosion of Cu-Ni Alloy in Liquid/Solid Two Phase Flow through Pipe白铜在液固双相流中的冲刷腐蚀研究
16.Corrosion Behavior of Carbon Steel and Copper in Different Soil Solutions碳钢和纯铜在试验土壤中的腐蚀研究
17.Study on galvanic corrosion of copper and A_3 steel in NaCl solutionNaCl溶液中铜和A_3钢接触腐蚀的研究
18.Effect of Inhibitior HEDP-ATMP-TTA on Corrosion of HSn70-1A Copper-alloyHEDP-ATMP-TTA缓蚀剂对HSn70-1A铜合金腐蚀行为的影响

相关短句/例句

copper strip corrosion铜片腐蚀
1.In this paper, the NC-L type bi-functional absorbent was used in LPG unit, Aromatic Plant, YPC for solving the copper strip corrosion problem of produced automotive liquified petroleum gas.针对扬子石化股份公司芳烃厂液化气装置生产的车用液化气钢片腐蚀不合格的问题,采用NC-L型双功能吸附剂,有效地脱除车用液化气中的H_2S和HCl,使其铜片腐蚀指标合格,取得了良好的经济和社会效益。
2.The copper strip corrosion qualification for FCC gasoline is one of the national standards.催化裂化汽油铜片腐蚀合格是重要的国标之一 ,但由于将重油作为催化裂化原料而使部分催化裂化汽油铜片腐蚀不合格。
3)copper corrosion铜片腐蚀
1.The off-spec copper corrosion resulting from emulsification caustic carry over can be avoided while keeping product sulfur within specification该工艺与现有的静态混合器、填料塔、塔板塔等工艺比较,具有二相混合强度低而接触面积大,脱硫率高的显著特点,在使产品总硫合格的前提下,可有效地避免乳化带碱引起的产品铜片腐蚀不合格。
2.On the basis of FCC gasoline treatment processes,the causes of off-specification of copper corrosion test of gasoline were analyzed,and the differences in sulfur distribution in FCC gasoline with different corrosivities were investigated.从催化裂化汽油的精制工艺入手,分析了造成汽油铜片腐蚀不合格的原因,对汽油中的活性硫化物如元素硫、硫化氢等进行了深入研究,并对如何避免汽油铜片腐蚀的发生提出了建议。
3.The results showed that the mass concentration of sulphur in LPG was dropped from 10mg/m3 to 5mg/m3,the copper corrosion of LPG declined from grade 2~3 to 1.运行结果表明,采用NF-Q精脱硫剂对重整液化气进行脱硫后,液化气总硫质量浓度由10 mg/m3下降为5 mg/m3,铜片腐蚀由2~3级下降为1级,满足GB 1174—89的要求。
4)bronze corrosion青铜腐蚀
5)copper engraving, etched copper-plate腐蚀铜版
6)Copper plate corrosion铜板腐蚀