1)TP347H steelTP347H钢
1.Investigation of high-temperature steam oxidation for TP347H steelTP347H钢高温水蒸气氧化研究
2.The results showed that the rupture life of TP347H steel after adding 0.3%(质量分数)的Ce,用25 kg真空感应炉在氩气保护下熔炼,研究了Ce对TP347H钢高温持久性能等的影响。
英文短句/例句
1.Investigation of high-temperature steam oxidation for TP347H steelTP347H钢高温水蒸气氧化研究
2.Research and Development of Large-sized Heavy-wall TP347H Stainless Steel Pipe大直径厚壁TP347H不锈钢管的研制与开发
3.Researches on the early failure of TP347H and 12Cr1MoV dissimilar steel welded jointsTP347H与12Cr1MoV异种钢焊接接头早期失效研究
4.Effect of Nitrogen on Tensile Strength at Room Temperature and Creep Rupture Life of TP347H Heat-Resistant Austenitic Stainless Steel氮对TP347H耐热奥氏体不锈钢室温拉伸和高温持久性能的影响
5.Leakage Analysis of Reheater TP347H Tube of a Power Plant某电厂再热器TP347H管泄漏原因分析
6.Effect of Microstructure to Corrosion Properties for Welded Joint of P91+SUS347 SteelP91+TP347H焊接异质接头晶间腐蚀研究
7.CORROSION CHARACTERS OF TP347H STEEL UNDER ATMOSPHERE OF SUPERHEATERS OF BIOMASSBURNED BOILERS(Ⅱ)TP347H在生物质锅炉过热器气相条件下的腐蚀特性(Ⅱ)
8.CORROSIVE CHARACTORS OF TP347H STEEL IN SUPERHEATER'S ATMOSPHERE OF BIOMASS-BURNED BOILERTP347H在生物质锅炉过热器气相条件下的腐蚀特性(Ⅰ)
9.High Temperature Steam Oxidization Resistance of TP347H Panel Division Super-heater Tubes for 600MW Super-critical Boiler600MW超临界锅炉TP347H屏式过热器管高温蒸气氧化腐蚀探讨
10.corrosion resistant stee抗腐蚀钢, 耐蚀钢, 不锈钢
11.dead-hard steel极硬钢, 高硬钢, 高强钢
12.Stainless Steel/Steel Dome Head不锈钢/钢 圆头型
13.Stainless Steel/Steel Countersunk不锈钢/钢 沉头型
14.Bessemer mild steel贝塞麦钢, 酸性钢
15.Stainless Steel/Steel Standard不锈钢/钢 标准型
16.cold-rolled carbon steel冷轧碳钢, 低碳钢
17.notch ductile steel耐冲击钢, 韧性钢
18.dead-melted steel镇静钢, 全脱氧钢
相关短句/例句
TP347H stainless steelTP347H不锈钢
1.Through tests and analysis of welds between TP347H stainless steel and12CrMoWVTiB (G102) heat-resistant steel after 55 221.64h的TP347H不锈钢与12Cr2MoWVTiB(G102)耐热钢异种钢焊接接头进行了试验研究,结果表明,G102侧热影响区为整个焊接接头的薄弱环节,鉴于该类焊接接头G102侧热影响区冲击值很低,建议尽早更换。
3)TP347H tubeTP347H钢管
1.Analysis on burst of TP347H tube for power station boiler;电站锅炉用TP347H钢管爆裂分析
4)Stainless Steel TP347HTP347H不锈钢管
5)Austenite Heat Resistant Steel TP347H奥氏体耐热钢TP347H
1.Effect of Boron on Hot Workability, Structure and Mechanical Properties of Austenite Heat Resistant Steel TP347H;硼对奥氏体耐热钢TP347H热加工性、组织和力学性能的影响
6)austenite stainless steel(TP347H)奥氏体不锈钢(TP347H)
延伸阅读
45钢和40Cr钢调质的热处理工艺45钢40Cr钢调质调质是淬火加高温回火的双重热处理，其目的是使工件具有良好的综合机械性能。调质钢有碳素调质钢和合金调质钢二大类，不管是碳钢还是合金钢，其含碳量控制比较严格。如果含碳量过高，调质后工件的强度虽高，但韧性不够，如含碳量过低，韧性提高而强度不足。为使调质件得到好的综合性能，一般含碳量控制在0.30~0.50%。调质淬火时，要求工件整个截面淬透，使工件得到以细针状淬火马氏体为主的显微组织。通过高温回火，得到以均匀回火索氏体为主的显微组织。小型工厂不可能每炉搞金相分析，一般只作硬度测试，这就是说，淬火后的硬度必须达到该材料的淬火硬度，回火后硬度按图要求来检查。工件调质处理的操作，必须严格按工艺文件执行，我们只是对操作过程中如何实施工艺提些看法。1、45钢的调质45钢是中碳结构钢，冷热加工性能都不错，机械性能较好，且价格低、来源广，所以应用广泛。它的最大弱点是淬透性低，截面尺寸大和要求比较高的工件不宜采用。45钢淬火温度在A3+(30~50)℃，在实际操作中，一般是取上限的。偏高的淬火温度可以使工件加热速度加快，表面氧化减少，且能提高工效。为使工件的奥氏体均匀化，就需要足够的保温时间。如果实际装炉量大，就需适当延长保温时间。不然，可能会出现因加热不均匀造成硬度不足的现象。但保温时间过长，也会也出现晶粒粗大，氧化脱碳严重的弊病，影响淬火质量。我们认为，如装炉量大于工艺文件的规定，加热保温时间需延长1/5。因为45钢淬透性低，故应采用冷却速度大的10%盐水溶液。工件入水后，应该淬透，但不是冷透，如果工件在盐水中冷透，就有可能使工件开裂，这是因为当工件冷却到180℃左右时，奥氏体迅速转变为马氏体造成过大的组织应力所致。因此，当淬火工件快冷到该温度区域，就应采取缓冷的方法。由于出水温度难以掌握，须凭经验操作，当水中的工件抖动停止，即可出水空冷（如能油冷更好）。另外，工件入水宜动不宜静，应按照工件的几何形状，作规则运动。静止的冷却介质加上静止的工件，导致硬度不均匀，应力不均匀而使工件变形大，甚至开裂。