纳米粉,nano-powder英语短句,例句大全

纳米粉,nano-powder
1)nano-powder纳米粉
1.The surface of polyester fabrics is treated with five kinds of nano-powders(ZnO,TiO_2,SiO_2,Al_2O_3,SnO_2)with four silane-coupling agents and four titanate-coupling agents,and then the permeation rate of ultraviolet radiation and the ability of photo catalyzing of the fabric are tested.分别使用4种不同的钛酸酯和硅烷偶联剂对涤纶织物进行不同纳米粉(ZnO、TiO2、SiO2、Al2O3、SnO2)的偶联整理,并测试了织物紫外线透过率和光催化等性能。
2.ZnO and ZrO_2 nano-powders were prepared by Polyglycol Method,using Zn(NO_3) and ZrOCl_2 as precursors.结果显示,采用聚乙二醇法制备了分散性较好的粒径约12 nm的ZrO2纳米粉体和粒径约50~75 nm的ZnO纳米粉体。
3.SnO 2 and TiO 2-SnO 2 nano-powders were prepared by stearic acid method.采用硬脂酸法分别制备了SnO2 纳米粉体及TiO2 SnO2 混合纳米粉 ,并应用XRD和TEM等分析方法对所得粉体进行了表征。

英文短句/例句

1.Microwave Synthesis of CoFe_2O_4 Nano-powders;微波合成CoFe_2O_4纳米粉体
2.On Content Measurement of Nanometer Powder in α-Al_2O_3 Nanometer Nickel-plated Layer;α-Al_2O_3纳米镀镍层中纳米粉含量测定方法的研究
3.Synthesis of MgAl_2O_4 Spinel Nannopowder by Sol-gel Process溶胶-凝胶法制备纳米镁铝尖晶石纳米粉
4.Preparation and Characterization of Rare Earth Doping YAG Phosphors and Y-TZP Nanopowder;稀土掺杂YAG荧光粉和Y-TZP纳米粉的制备及表征
5.State and prospect of nanoparticle preparation for laser ablation激光烧蚀法制备纳米粉的现状及前景
6.Study on Preparation and Properties of Nanoscale Energetic Materials;含能材料纳米粉体的制备和性能研究
7.Research on the Mechanism of Modifiing Cement-Based Materials by the Use of Nanopowders;纳米粉体改性水泥基材料机理的研究
8.Research on Synthesis of SrCO_3 and SrTiO_3 Nanopowders;纳米SrCO_3及SrTiO_3粉体的研制
9.Preparation of Nano-Sized BaTiO_3 Powders;纳米BaTiO_3粉体的制备研究
10.Preparation of Silica Nanoparticles from Waste Light Silicon Ash利用废弃微硅粉制备纳米SiO_2粉体
11.Cutting processing and equipment of the sub-nanometer ultra-fine wood flour亚纳米木粉粉碎工艺及设备构成原理
12.Thermal stability of composite of nanocrystalline WC powder and carbon nanotubes碳纳米管复合纳米碳化钨粉体的热稳定性
13.Synthesis and Characterization of ZnO Nanoparticles by Sol-Gel Method;溶胶—凝胶法制备纳米氧化锌粉体及纳米氧化锌粉体的表征
14.This augurs the change on the microscopic structure.这预示着纳米荧光粉微结构的变化。
15.Will long-term intake of nanometer pearl powder lead to concretion?长期服用纳米珍珠粉会不会产生结石？
16.Globular nanometer γ aluminum oxide powder was synthesized through detonation of aluminum nitrate.用爆轰法合成了纳米γ氧化铝粉体。
17.Developments in Preparation of Nanometer CeO_2纳米氧化铈粉体的制备技术研究进展
18.Advanced Sintering Technique of Nanometer Magnetic Powder──Explosive Consolidation纳米磁性粉末成形新工艺──爆炸烧结

相关短句/例句

nanometer powder纳米粉
1.MgAl2O4 spinel nanometer powders were synthesized via sol-gel process of aluminium isopropoxide that hydrated in the solution of magnesium nitrate with tetrahydrofuran being stabilizer.以四氢呋喃作稳定剂,通过异丙醇铝在硝酸镁溶液中水解的Sol-Gel过程合成了MgAl2O4尖晶石纳米粉体,采用DTA、XRD及TEM等分析手段研究了其前驱体的晶化过程和不同煅烧温度对尖晶石粉体晶粒尺寸及烧结性能的影响。
2.The crystallization process was studied for the VO2 nanometer powders prepared by a liquid phase hydrolysis method with VOSO4 as precursor, and the physical properties of the prepared powders were tested by means of TGA, DSC, XRD and TEM in this paper.研究了以VOSO4为前驱体,应用液相沉淀法制取VO2纳米粉的制粉技术以及VO2粉末的晶化过程,采用TGA,DSC,XRD,TEM等测试手段对所得粉的物理特性进行了测试分析。
3.Beginning with a brief description of the preparation and properties of rare earth compounds,thispaper compares and discusses the preparation methods and physical properties such as luminescence and catalysis of rare earth compounds nanometer powders.从稀土化合物的制备、性能出发,比较并讨论了稀土纳米粉体材料的各种制备方法,荧光、催化和光伏等物理特性,并对今后的研究重点和发展前景进行了展望。
3)nanoparticles纳米粉
1.Preparation of SiO_2 nanoparticles with alkoxide hydrolysis precipitation method;醇盐水解沉淀法制备二氧化硅纳米粉
2.High-purity tantalum oxide nanoparticles were prepared by using tantalum ethoxide as materials through the following three processes,such as hydrolysis,dryness and calcining.以自制高纯乙醇钽为原料,通过水解、干燥与煅烧生产粒度约35nm的高纯Ta2O5纳米粉。
3.The five copper heat pipes,with the same long of 800mm,internal diameter of 10mm and water of 10mL,were tested under the same experimental conditions,one of which is traditional heat pipe;other four of which,their working matters(water) begin added ZnO,SiO2,Al2O3 and TiO2 nanoparticles respectively,are new-type of heat pipes.在普通热管的工质(水)中分别加入ZnO,SiO2,Al2O3和TiO2纳米粉制成了4根新型热管与1根普通热管,共5根热管,均由铜管制成,长度为800 mm,外径12 mm,内径为10 mm,加入水10 mL。
4)Nano/nano-phased powder纳米粉/纳米相粉
5)Nanometer Powder纳米粉体
1.Application of supercritical fluids drying technology in the preparation of nanometer powder;超临界流体干燥技术在纳米粉体制备中的应用
2.Agglomerate mechanism of nanometer powders in atmosphere and methods of preparation of nan-agglomerate nanometer powders;纳米粉体大气环境团聚机理及无团聚纳米粉体的制备
3.The study of preparing Y2O3 stabilized ZrO2 nanometer powder in stearic acid sol by microwave heating;溶胶凝胶-微波加热技术制备Y_2O_3稳定ZrO_2纳米粉体的研究
6)aluminum nanopowders纳米铝粉
1.Aluminum nanopowders were synthesized by high frequency induction evaporation condensation method,and aluminum nanopowders was treated by passivation in air.采用高频感应线圈加热,以蒸发-冷凝法制备了纳米铝粉,用空气进行钝化处理,得到有钝化层保护的纳米铝粉。