1)porcelain powder烤瓷粉
1.The experimental results indicted the elementary frit was mixed with the frit containing leucite 20%～25%, then porcelain powder was synthesized, and the heat compatibility between the porcelain powder and metal was established.试验结果表明,采用多相成核方法可得到含有大量白榴石晶体的熔块,在基础熔块中加入20%～25%的白榴石熔块后可获得与金属合金有良好热匹配的烤瓷粉。
2.The dental zirconia-leucite composite porcelain powder was synthesized by the solid-state method using nano-zirconia and potassium carbonate as raw materials.以钾长石、碳酸钾和纳米氧化锆为主要原料,通过高温同相法,一次性合成了一种牙用白榴石-氧化锆复合烤瓷粉。
英文短句/例句
1.Preparation and Characterization of Veneer Porcelain for Alumina All-Ceramic Crown氧化铝全瓷冠用烤瓷粉的制备及表征
2.Effects of Zirconia on the Properties of Leucite-based Porcelain Powder氧化锆对白榴石基烤瓷粉性能的影响
3.Clinical evaluation of the effect of gold alloy and Ni-Cr alloy porcelain fused metal crown restorations贵金属烤瓷与镍铬合金烤瓷修复体的效果评价
4.dish ,baking or roastin,g of porcelain or china烘烤或焙烧盘碟,瓷或白坯瓷制
5.dish ,baking or roasting, of ceramic other than porcelain or china烘烤或焙烧盘碟,除瓷或白坯瓷外的陶瓷制
6.Influnce on Porcelain Repareing from Different Ceramic Surface Treatments;瓷表面粗化处理对烤瓷修复体崩瓷修补的影响
7.Sift together the cake flour, baking powder and vanilla powder and set aside.低筋粉，烤粉和香草粉混合过筛备用。
8.Combine flour, baking powder, baking soda, cinnamon and salt. Set aside.混合面粉，烤粉，小苏打，肉桂粉和盐，备用。
9.The other three kinds are the exquisitely wrought blue and white ware, the famille rose porcelain and the colored glaze porcelain.另外有青花玲珑瓷，粉彩瓷和颜色釉瓷。
10.sausage baked in batter.香肠裹在面粉中烘烤。
11.Preheat an oven to 180C/350F. Shif the flour, baking powder and pudding powder(of milk powder if used).预热烤箱到180C.把面粉，烤粉，和布丁粉或是奶粉混合过筛备用。
12.Influence of Galvano-ceramic and Precious Metal-ceramic Crowns on Magnetic Resonance Imaging金沉积烤瓷冠和贵金属烤瓷冠对磁共振图象的影响
13.A Study of Metal-ceramic Bonding on a New Type of Cobalt-chromium Alloy for Both Dental Framework and Porcelain Fused to Metal;新型牙用烤瓷支架钴铬合金金瓷结合的研究
14.Study on Metal-ceramic Bonding Strengths of Several Base Metal-ceramic Alloys Frequently Used Clinically;牙科常用非贵烤瓷合金金—瓷结合强度的研究
15.The Study of New Nickle-Ceramic Alloy and the Combination of Ceramic to Metal;新型镍基牙科烤瓷合金金瓷结合性能的研究
16.A Comparative Study on Five Frequently Used Alloys Bond to Porcelain;五种常用烤瓷合金金瓷结合强度的比较研究
17.Porcelain Fused to Pure Titanium and Effect of Ti Surface Modification on Ti/Porcelain Strength纯钛烤瓷及钛表面改性对钛/瓷结合强度的影响
18.Study on the Effects of the Fusing Parameter on the Bonding Strength of Titanium-porcelain烤瓷烧结参数对钛—瓷间结合强度影响的研究
相关短句/例句
porcelain[英]['p?:s?l?n][美]['p?rsl??n]烤瓷
1.Interface microstructure and mechanical properties of Ni-Cr alloy porcelain materials;Ni-Cr合金烤瓷材料界面组织结构和力学性能
2.Interface reaction mechanism of porcelain fused to Ni-Cr alloy;Ni-Cr合金烤瓷界面反应微观机理
3.Clinical observation of restoring single front missing tooth with improved porcelain-fused-to adhesion fixed bridge;改良式烤瓷粘结桥修复单个前牙缺失的临床观察
3)ceramic[英][s?'r?m?k][美][s?'r?m?k]烤瓷
1.Effect of two kind of methods of color selection on the clinic ceramic restoration under the standard lightness;标准光源下两种选色方法对烤瓷修复的影响
2.Effects of different methods of shade selection colormeter on the ceramic restoration;应用不同选色方法对临床烤瓷修复效果的影响
3.Objective To discuss the restoration of defected surface of subgingival residual roots and crowns caused by violence or dental caries with resin post core and titanium alloy ceramic.目的探讨因外伤或龋病导致的残根残冠缺损面位于龈下3 mm左右时进行树脂核桩加钛合金烤瓷冠修复问题。
4)Porcelain furnace烤瓷炉
5)PFM烤瓷修复
1.PFM nickel-chromium alloy of clinical application;镍铬合金烤瓷修复体的临床应用
2.Effect of 64 PFM cases supported by screw posts for the residual dental roots of posterior teeth;利用螺纹桩对64例后牙残根烤瓷修复的疗效观察
3.PFM technology is currently widely used in clinical, at the same time there have been some cause for concern, such as a few months after PFM restorations the adjacent gingival tissue swelling, shaded black, and even gingival atrophy, root exposure, what mentioned above seriously affect the effect of remediation.唇侧龈组织的美感是前牙美观不可分割的一部分,随着美学修复的倡导,金属烤瓷修复后牙龈变色的问题得到人们的普遍重视,但其原因在口腔修复界一直存在争议。
6)PFM烤瓷冠
1.Using the PFM to cure individual scissors bite of adults;烤瓷冠修复在治疗后牙正锁中的临床应用18例分析
2.Effect of two different PFM on periodontal tissue;两种不同烤瓷冠对牙周组织的影响
3.The clinical effects about restoring accidental porcelain fracture of PFM with M·L·Primer and Solidex;金属粘接剂及瓷聚合体树脂修复金属烤瓷冠意外崩瓷的临床应用
延伸阅读
烤瓷粉分子式：CAS号：性质：在牙科烤瓷工艺中，进行烧结加工制作烤瓷修复体所采用的粉状瓷料。有长石质烤瓷粉和氧化铝质烤瓷粉两大类。前者包括体瓷和釉瓷。体瓷由长石、石英、白陶土、硼砂、硅石、氧化铝、着色剂、结合剂等组成；釉瓷由石英和硼砂等组成。而氧化铝质烤瓷粉除上述各组分外，还含有40％～50％的α-Al2O3结晶体。用烤瓷粉制作的烤瓷修复体光学性能好，色泽稳定，生物学性能佳，但机械强度较差。用于制作烤瓷全冠、瓷牙、嵌体、烤瓷桥等。