1)heating oxygenation加热氧化
2)slight oxidization heating少氧化加热
1.In the paper,the author presents the heat supply features and combustion conditions of slight oxidization heating,and analyzes,through simulating calculation of combustion,the effects of air consumption coefficient( n <1) on the furnace atmosphere(CO/CO 2、H 2/H 2O)and the conditions for realizing slight oxidization heating.分析了少氧化加热的供热特点及燃烧条件。
3)electrothermal oxidation电加热氧化
1.The preparation, structure and photocatalytic properties of titanium dioxide film formed by electrothermal oxidation of metal titanium were investigated by XRD, SEM and UV spectroscopy measurements.应用在空气中电加热氧化的方法在金属钛表面制备了TiO2薄膜并通过XRD, SEM 以及UV方法分别研究了其晶相结构、表面形貌及光催化活性。
4)nonoxidizing heating无氧化加热
英文短句/例句
1.direct-fired scale-less of free heating furnace敞焰少无氧化加热炉
2.Basic Study on Making Non-Oxidizing Atmosphere for Hot-Work by Circulating;循环法制备无氧化热加工气氛基础研究
3.Sometimes either the compression or the sintering may be omitted. During the heating it is generally necessary to protect the material from oxidation by atmospheric air, by the use of non-oxidizing gas.偶尔亦可不进行压制或无须烧结。在加热时一般必须使用非氧化气体．以防止粉末被空气氧化。
4."The non-oxidizing zone is consisted of entry sealed room, waste gas preheating zone, direct heating zone, and furnace nozzle and flue gas exhausting system. "无氧化段由入口密封室,废气预热区,直接加热区,炉喉,废气排放系统组成
5.deaerating heater除气加热器除氧加热器
6.impregnate with thorium oxide to increase thermionic emission.注入镀氧化物使增加热电子发射。
7.Thermodynamic Analysis of CO_2 Hydrogenation to Formic Acid;二氧化碳加氢合成甲酸的热力学分析
8.Synthesis and Characterization of TiO_2 Nano Powders by Pyrogenation-with-Sugar-Protection Method二氧化钛纳米粉体的加糖热解法制备
9.INFLUENCE OF MICROWAVE HEATING ON THE OXIDATIVE STABILITY OF PEANUT OIL微波加热对花生油氧化稳定性的影响
10.High Purity Magnesia Preparation from Mg(HCO_3)_2 with Ethanol Addition重镁水添加乙醇热解制备高纯氧化镁
11.EFFECT OF HEAT TREATMENT ON SURFACE QUALITY OF DIAMOND TOOL TURNED OFHC(UT2)热处理对无氧铜超精加工表面质量的影响
12.in chemistry; heat a substance so that it oxidizes or reduces.在化学中；给一种物质加热以便使它氧化或还原。
13.Parameter Optimization in Thermal Wave NDT with Uniform Heating基于持续加热的热波无损探伤参数优化
14.A flaky oxide film formed on a metal, as on iron, that has been heated to high temperatures.氧化层给金属高温加热生成的片状氧化物，如铁上
15.Phase Transition Vanadium Oxide Thin Films Fabricated by Facing Targets Magnetron Sputtering with Low Temperature Thermal Oxidation用对靶磁控溅射附加低温热氧化处理方法制备相变氧化钒薄膜
16.Thermal Oxidation Mechanism of Jet Fuel and Research Advance of Additives Improving Oxidative Stability喷气燃料热氧化机理及氧化稳定添加剂的研究进展
17.Research on Thermo-plasticity Precision Forming Without or Little Oxidation System in Nitrogen-based Atmosphere;热塑性精成形氮基气氛少无氧化系统的研究
18.Fabrication of Agglomerate-free ZnO Nanoparticles by Electrospraying and Subsequent Two-step Heat Treatment电喷雾和二步热处理制备无硬团聚纳米氧化锌
相关短句/例句
slight oxidization heating少氧化加热
1.In the paper,the author presents the heat supply features and combustion conditions of slight oxidization heating,and analyzes,through simulating calculation of combustion,the effects of air consumption coefficient( n <1) on the furnace atmosphere(CO/CO 2、H 2/H 2O)and the conditions for realizing slight oxidization heating.分析了少氧化加热的供热特点及燃烧条件。
3)electrothermal oxidation电加热氧化
1.The preparation, structure and photocatalytic properties of titanium dioxide film formed by electrothermal oxidation of metal titanium were investigated by XRD, SEM and UV spectroscopy measurements.应用在空气中电加热氧化的方法在金属钛表面制备了TiO2薄膜并通过XRD, SEM 以及UV方法分别研究了其晶相结构、表面形貌及光催化活性。
4)nonoxidizing heating无氧化加热
5)scale-less or free heating少无氧化加热
6)high temperature heat treatment under oxidation高温氧化加热法
延伸阅读
锻坯少无氧化加热 使锻坯表层没有或只有少量氧化皮的锻坯加热工艺。这种加热法特别适宜于同少无切削加工和精密锻造配套使用。影响氧化的主要因素是炉气成分、加热温度和加热时间。①炉气成分:炉气中的O2、CO2、H2O等属于氧化气氛，易使金属氧化；CO、H2、Cn H m、N2等分别是还原气氛和惰性气体，可防止氧化。②加热温度：温度越高，氧化也越激烈。钢在500℃下氧化甚缓,600～700℃氧化加快，900℃以上急剧氧化。以900℃的氧化指数为1,则1000℃时增加为2,1100℃时为3.5，1300℃时为7。③加热时间：在同样温度和气氛条件下，氧化随时间成正比增加。在合理的加热温度条件下,减少氧化的途径是:缩短坯料在炉内停留时间，勤装料、勤出料；尽量减少多余的空气，严格控制通风量，减少漏风，保持炉内还原性气氛。 少氧化和无氧化加热有多种方法。 保护气氛下电阻炉加热 这是最方便的无氧化加热方法，但需要大的电源，热效率低，加热缓慢。 保护气氛下马弗炉加热 在马弗式电阻炉中通入保护气氛加热。在没有充分的电源时,仍用火焰炉加热,但需将锻坯放在马弗罩中使之与氧化性的炉气隔离。炉气将马弗罩加热至高温，再由马弗辐射加热锻坯。马弗罩用碳化硅、刚玉等耐高温材料制成，寿命较短，限制了这个方法的应用。 盐浴加热和玻璃浴加热 用熔融的金属盐 (一般用氯化钡和氯化钠混合物)或玻璃将锻坯与空气隔离,用电阻加热盐浴。锻坯上的盐膜或玻璃还能保护金属出炉后不受二次氧化，但盐或玻璃可能留存在模膛内造成锻件缺陷和损坏模具。另外，这种方法的热效率也较低。盐浴需要好的通风装置以排除有害健康的盐蒸气（见盐浴炉）。 浮动粒子炉加热 用石墨、石英砂、刚玉粒代替熔盐作加热介质。工作时粒子形成悬浮状态的流床，锻坯在其中加热。采用这种方法可避免盐浴加热的缺点，但需要有鼓风装置和保护气体。 涂保护覆盖层后加热 在锻坯加热前用水玻璃、铝粉、镁砂、硼酸盐等涂料浸渍或涂刷，形成保护性覆盖层，然后在火焰炉加热。这种方法简单，但保护不完全可靠。 快速电感应加热和电接触加热 这类高速加热设备主要用在锻造生产线中，从坯料开始加热到锻成成品仅需几分钟；虽不用保护气体，氧化也较轻微。对于大批量生产的中、小型精密锻件，这是有更大发展前途的加热方法。它的主要缺点是不适用于多品种、小批量生产。 敞焰少无氧化加热 敞焰少无氧化加热可用于大件生产,加热方法可以是间歇式的也可以是连续式的,且不需要大的电源，是一种最常用的少无氧化加热方法。加热时，将工件直接放在有还原性气氛的火焰炉中，当钢锻坯加热到1200℃,炉气中小于0.3,小于0.8时，氧化与还原作用平衡（图1）, 可以获得少无氧化的气氛，钢坯不产生氧化或仅产生轻微氧化。图2为敞焰少无氧化加热炉的原理。控制助燃空气使煤气燃烧不完全，以产生较多的CO和H2，使炉气成为少无氧化气氛。另在炉膛上部补充通入预热到300～500℃的二次空气，煤气在炉膛上部二次燃烧，提高预热温度，使热量辐射给炉底的钢坯。较高的炉膛结构使上层的氧化性炉气不易到达钢坯加热区。这种加热方法的缺点是热效率较普通的火焰加热炉低，操作复杂。