1)cold deformation冷变形
1.Investigation on cold deformation and dynamic recrystallization of Cu-Ni-Si-Ag alloy;Cu-Ni-Si-Ag合金冷变形及动态再结晶研究
2.Effect of cold deformation and tempering on ductility of low carbon martensite steel;冷变形低碳马氏体钢的回火塑性
3.Effects of Cold Deformation on Super-elasticity and Microstructure of TiNiCr Shape Memory Alloys;冷变形对TiNiCr形状记忆合金超弹性和组织的影响
英文短句/例句
1.Influence of Cold Deformation on Shape Recovery Ratio and Transformation Temperature of FeMnSiCrNi Shape Memory alloys冷变形对FeMnSiCrNi合金形状恢复率和转变温度的影响
2.Study on the Microstructure and Texture of the Cold-rolled Eutectoid Steel冷变形共析钢的显微组织与织构探讨
3.The Study on Austenite Continuous Cooling Transformation and Cold Deformation Character of CSP Low Carbon Stell;CSP低碳钢奥氏体连续冷却转变及冷变形特性研究
4.degree of cold work冷加工(材料变形)程度
5.Study on Deformation Laws and Forming Process Simulation for Cold Ring Rolling;环件冷辗扩变形规律和工艺模拟研究
6.Analysis for Distortional Buckling of Cold-formed Thin-walled C-section Steel in Bending;冷弯薄壁C形槽钢受弯畸变屈曲分析
7.Study on Extrusion Deformation Laws and Technics for the Covering Element;罩体冷挤压成型变形规律及工艺研究
8.Discussion on Prediction Accuracy of Yield Stress Model of Cold Rolling Mill冷连轧变形抗力模型预报精度的探讨
9.Behaviour of Thermal Deformation of Steel Cr5 for Cold Working RollCr5型冷轧工作辊用钢的热变形行为
10.Effects of Cold Rolling Reduction on Microstructure of Ti+P-IF Steel冷轧变形量对Ti+P-IF钢微观结构的影响
11.Microstructure and Deformation Mechanism of Cold-Rolled TRIP800 Steel冷轧TRIP800钢的组织性能和形变行为
12.Influences of Deformation and Cooling Rate on the Microstructure Evolution of T91 Heat-resistant Steels;变形和冷却速度对T91耐热钢组织形成的影响
13.Continuous cooling transformation behaviour in the undeformed and deformed conditions of cold heading steel铆螺钢不变形和变形条件下连续冷却的相变行为
14.The Study of Phase Transformation during Continuous Cooling and Deformation of Nb Micro-alloyed Steel;Nb微合金钢形变连续冷却过程中的相变研究
15.Influence of Cooling Rate on Microstructure Evolution Due to Deformation Induced Ferrite Transformation in Vanadium Microalloyed Steel冷速对钒微合金化钢形变诱导相变组织的影响
16.Effect of Molybdenum on Continuous Cooling Transformation of Ship Plate Steel with High Strength钼对高强度船板钢变形后连续冷却转变的影响
17.Research on hot deformation resistance and continuous cooling transformation of ultra-low carbon bake hardening steels超低碳BH钢变形抗力和连续冷却转变热模拟
18.Effect of the Hot Deformation on Continious Cooling Transformation Curve for DP600 Steels热变形对DP600汽车用钢连续冷却转变曲线的影响
相关短句/例句
cold working冷变形
1.The influences of various cold working on properties of Cu-0.研究结果表明,合金经950℃、1 h固溶处理后施以不同程度冷变形,再进行480℃时效处理,比合金固溶后直接时效可显著提高合金的电导率和显微硬度;随变形量逐渐增大,合金强度不断升高,抗拉强度最高可达645 MPa,而延伸率和导电率略有降低。
2.This paper was dealt with the influnce of aging parameter and cold working on properties of Cu-0.结果表明合金经950℃×1h固溶后,在480℃时效可获得较高的导电率和硬度;时效前对合金施以冷变形可以加速时效初期第二相的析出,并显著提高其电导率和硬度,60%变形合金 480℃×2h时效处理后,导电率和显微硬度分别为83。
3.The precipitation process of secondary phase can be accelerated by cold working before aging treatment, and the pinning effect of the precipitates on the dislocations gre.时效前冷变形能大大加快析出相的析出,析出相对位错的钉扎作用强烈阻碍合金再结晶的形核和长大,使合金产生明显的时效硬化。
3)Cold deforming冷变形
1.Study on the cold deforming and aging characteristics of Cu-Cr-RE alloy;Cu-Cr-RE合金的冷变形及时效特性研究
2.The results show that the process of precipitating can be accelerated as large amounts of cold deforming before aging.结果表明 ,合金经大幅度冷变形再时效可加速析出过程 ,析出物具有与 δ- Ni2 Si相似的正交晶格 ,时效时由于析出相变而形成了较特殊的再结晶过
4)cold-drawing deformation冷拉形变
1.The compound strengthening and toughening of sub-critical quenching and cold-drawing deformation on 20CrMnMo steel was studied.对20CrMnMo进行亚温淬火热处理和冷拉形变的复合强韧化研究。
5)cold rolling冷轧变形
1.The effect of cold rolling deformation prior to aging on the strengthening of a maraging steel was investigated.系统研究了预先冷轧变形对马氏体时效钢强化的影响,研究结果表明:510℃×3 h时效引起的强度净增加值恒定,与冷轧变形量无关,最终的强度为:σ=σ0+ΔσCR+ΔσAge,即初始强度、冷加工强化和时效强化的叠加,其中只有冷加工强化ΔσCR随变形量变化。
2.The article introduces microstructure evolution and mechanical hardening of three different kind steels during cold rolling.本文介绍了三种钢在冷轧变形过程中的组织演变和形变强化规律，发现三种钢具有不同的形变强化规律。
6)cold upsetting deformation冷压形变
延伸阅读
冷变形冷变形cold deformation 属塑性加工的重要方式，用于生产薄板、带卷、箔材、线材、管材、棒材和一些五金零件。冷变形制品表面光洁，尺寸精确，形状规整。 (妻燕雄)lengbianxing冷变形(eold deformation)金属材料在低于再结晶温度下的塑性变形。在金属塑性加工领域中通称冷加工。冷变形时工件发生加工硬化，但不发生再结晶软化。 冷变形使工件的组织和性能发生以下的变化: (1)晶粒形状改变。随着冷变形的进行。晶粒沿最大主变形方向拉长或压扁，变形达到相当程度后，形成纤维状组织(见纤维组织)。由于变形的不均匀性，工件内晶粒被拉长、压扁或呈纤维状的程度也不完全一致。 (2)晶粒内可能出现滑移带和孪生带，且空位、间隙原子、位错、层错增多，位错的增殖、交截(见位错交截)、塞积(见位错塞积)和缠结(见位错缠结)增多，位错密度由lxlo6em一2逐步增加到lxlo‘o~10‘2。m一2，金属的内能增加，从而使金属的强度和硬度以及全属的变形杭力等指标提高，延伸率等塑性指标降低，一些理化性能也发生变化，如电阻率增大，抗蚀性下降等。 (3)出现变形织构。在较大的冷变形程度下，金属各晶粒的位向从杂乱无序的随机状态逐渐转变为有序状态，即通称的择优取向。这就引起工件各方向上的性能发生差异，即各向异性。各向异性的程度即织构的强弱与变形量的大小、金属的成分和原有的组织状态有关。 (4)晶间和晶内发生破坏。冷变形导致位错塞积，当其应力值大于金属断裂强度时则形成裂纹和空洞，晶内或晶间联系遭到破坏，甚至发生断裂。 为了恢复冷变形金属的塑性、修复破坏、降低变形抗力和强度，根据金属的性质和生产工艺条件，在工件的冷变形量达到适当程度时，进行软化退火或再结晶退火(见低温退火)或回复，以控制工件的性能或有利于继续变形。 冷变形时的功，一部分消耗于工件与工具间的摩擦，一部分消耗于使工件产生塑性变形。后者中的80%左右转化为热，使工件温升及散失于周围介质中，约20%转化为金属的内能，储存于工件内，是以后热处理时组织变化的驱动力之一。冷变形给金属引入大量的晶体缺陷，如空位、位错、层错等，与这些缺陷相伴生的能量是上述储存能的主要形式，很少的一部分储存能以残余弹性应变形式存在。 冷变形如冷轧、冷拔、冷冲、冷锻、冷挤压等是金