1)creep crack蠕变裂纹
1.Studies were made on the nucleation of creep cavities and propagation of creep cracks in steel 20Cr11MoVNbNB at 550-650℃.研究了20Cr11MoVNbNB马氏体热强钢在550—65℃范围内蠕变孔洞的形成及蠕变裂纹的发展发现蠕变孔洞主要在原奥氏体晶界和原板条马氏体边界上的淬火未溶大颗粒Nb（C，N）及M23C6碳化物处形成，孔洞在原奥氏体晶界形成倾向不占优势：蠕变裂纹沿垂直应力方向横穿原奥氏体晶界及原板条马氏体边界向晶内扩展，最终导致穿晶断裂。
2.Because the pendent reheater tubes were subjected to thermal shock of steam blown by a sootblower during service,the thermal fatigue crack on outside surface was caused,and the creep crack adjacent to inner surface subsequently appeared.管材在运行中遭受吹灰蒸汽的热冲击,外壁因此出现热疲劳裂纹,随后内壁金属衍生出蠕变裂纹。
英文短句/例句
1.Numerical Simulation Analysis of the Creep Crack Characteristics of 2.25Cr1Mo Steel2.25Cr1Mo钢蠕变裂纹特性数值模拟分析
2.The analytical investigation of nonlinear creep crack growth is in its infancy and much remains to be learned and done.对于蠕变裂纹扩展的分析研究还是处于初期阶段，还有许多事情有待于认识和完成。
3.Study on the High-temperature Creep Behavior and the Estimation of Creep Crack Parameter C～* of Cracks in Bi-material CT Specimen;双材料CT试样裂纹高温蠕变行为的研究与蠕变断裂参量C～*的估算
4.Analysis of Strength Factor for Non steady Creeping Crack Tip Field非稳态蠕变二维裂纹尖端场强近似分析
5.Room Temperature Creep and Its Effect on Fatigue Crack Growth of Structural Steels;结构钢的室温蠕变及其对疲劳裂纹扩展的影响
6.Crack-tip Fields in Creep Damage Materials and Acoustic Detection of Mesodamage;蠕变损伤裂纹尖端场与细观损伤的声学探测
7.Numerical Simulation Analysis of Crack Opening of 1.25Cr-0.5Mo under Fatigue-Creep Interaction蠕变条件下1.25Cr-0.5Mo钢疲劳裂纹扩展数值模拟分析
8.STUDY OF CHARACTERISTICS OF MODE Ⅱ PROPAGATION CRACK TIP FIELD IN CREEPING MATERIALS WITH HARDENING EFFECT蠕变硬化材料中Ⅱ型扩展裂纹尖端场特性研究
9.Studies on Crack Propagation under Fatigue-creep Combined Action of 316L Steel at High Temperature;316L钢高温疲劳蠕变共同作用下裂纹扩展速率研究
10.Room Temperature Creep at Crack Tip in SUS304 Stainless Steel and Its Influence on Fatigue Crack Growth;SUS304不锈钢裂纹尖端的室温蠕变现象及其对疲劳裂纹扩展行为的影响
11.Study of cold crack initiation and propagation of compacted graphite iron weld蠕墨铸铁同质焊缝冷裂纹启裂与扩展研究
12.testing methods for creep rupture of adhesive bonds粘合剂蠕变断裂的试验方法
13.SOME CRITICAL ISSUES IN CREEP AND FRACTURE ASSESSMENT AT HIGH TEMPERATURE高温蠕变与断裂评价的若干关键问题
14.They are fatigue cracks which is mainly caused by alternating stress.叶片裂纹是疲劳裂纹,主要由交变应力引起。
15.Creep Rupture Behavior of a Cast Ni-base Superalloy at High Temperature一种铸造镍基高温合金的高温蠕变断裂行为
16.Steady Creep Rate and Rupture Life for 2.25Cr-1Mo Steel2.25Cr-1Mo钢稳态蠕变速率和断裂寿命的研究
17.Creep Control Theory and Technology Research of Deep-Seated High Stressed Fracture Rock深井高应力裂隙围岩蠕变控制理论与技术研究
18.Creep Rupture Time Predication of a Superheater Wall in a Circulating Fluidized Bed Boiler循环流化床锅炉炉内屏式过热器蠕变破裂预测
相关短句/例句
creep crack growth rate (CCGR)蠕变裂纹扩展率
1.A theroretical equation for the calculation of creep crack growth rate (CCGR) has also been derived.根据局部损伤理论和相似原理 ,给出了蠕变裂纹启裂前的孕育上下限时间并推导了蠕变裂纹扩展率方程。
3)creep crack growth蠕变裂纹扩展
1.How to charcterize the creep crack growth with appropriate fracture mechanics parameters is rather challenging to the structural integrity assessment in the presence of weld interface.为此建议对ASTME145 7推荐的C 计算式进行修正 ,以正确演绎焊接试样的蠕变裂纹扩展行为。
4)torsional creeping crack扭转蠕变裂纹
5)creep-fatigue crack蠕变疲劳裂纹
6)creeping of fissure裂纹蠕动
延伸阅读
淬火裂纹和非淬火裂纹的特征及实例分析淬火裂纹是指在淬火过程中或在淬火后的室温放置过程中产生的裂纹。后者又叫时效裂纹。造成淬火开裂的原因很多，在分析淬火裂纹时，应根据裂纹特征加以区分。 一、淬火裂纹的特征 在淬火过程中，当淬火产生的巨大应力大于材料本身的强度时，便会导致裂纹产生。淬火裂纹往往是在马氏体转变开始进行后不久产生的，裂纹的分布则没有一定的规律，但一般容易在工件的棱角槽口、截面突变处形成。 在显微镜下观察到的淬火开裂，可能是沿晶开裂，也可能是穿晶开裂；有的呈放射状，也有的呈单独线条状或呈网状。 因在马氏体转变区的冷却过快而引起的淬火裂纹，往往是穿晶分布，而且裂纹较直，周围没有分枝的小裂纹。 因淬火加热温度过高而引起的淬火裂纹，都是沿晶分布，裂纹尾端尖细，并呈现过热特征：结构钢中可观察到粗针状马氏体；工具钢中可观察到共晶或角状碳化物。 表面脱碳的高碳钢工件，淬火后容易形成网状裂纹。这是因为，表面脱碳层在淬火冷却时的体积胀大比未脱碳的心部小，表面材料受心部膨胀的作用而被拉裂呈网状。 二、非淬火裂纹的特征 淬火后发生的裂纹，不一定都是淬火所造成的，一般可根据下面的特征来区分。 淬火后发现的裂纹，如果裂纹两侧有氧化脱碳现象，则可以肯定裂纹在淬火之前就已经存在。淬火冷却过程中，只有当马氏体转变量达到一定数量时，裂纹才有可能形成。与此相对应的温度，大约在250℃以下。在这样的低温下，即使产生了裂纹，裂纹两侧也不会发生脱碳和出现明显氧化。所以，有氧化脱碳现象的裂纹是非淬火裂纹。 如果裂纹在淬火前已经存在，又不与表面相通，这样的内部裂纹虽不会产生氧化脱碳，但裂纹的线条显得柔软，尾端圆秃，也容易与淬火裂纹的线条刚健有力，尾端尖细的特征区别开来。 三、实例分析 实例一： 40Cr钢制成的转子轴，经锻造、淬火后发现裂纹。裂纹两侧有氧化迹象，经金相检验，裂纹两侧存在脱碳层，而且裂纹两侧的铁素体呈较大的柱状晶粒，其晶界与裂纹大致垂直。结论：裂纹是在锻造时形成的非淬火裂纹。 当工件在锻造过程中形成裂纹时，淬火加热即引起裂纹两侧氧化脱碳。随着脱碳过程的进行，裂纹两侧的碳含量降低，铁索体晶粒开始生核。当沿裂纹两侧生核的铁素体晶粒长大到彼此接触后，便向离裂纹两侧较远的基体方向生长。由于裂纹两侧在脱碳过程中碳浓度的下降，也是由裂纹的开口部位向内部发展，因而为铁素体晶粒的不断长大提供了条件，故最终长大为晶界与裂纹相垂直的柱状晶体。