环烷酸腐蚀,naphthenic acid corrosion英语短句,例句大全

环烷酸腐蚀,naphthenic acid corrosion
1)naphthenic acid corrosion环烷酸腐蚀
1.Naphthenic acid corrosion is the tough problem in processing high-acidity crude.环烷酸腐蚀是炼制高酸值原油时遇到的一个难题。
2.Effective measures are recommended to control the naphthenic acid corrosion of the pipe,including selection of corrosion-resistant 316 or 316L steels and modification of tee construction.并提出了减缓阻垢剂进料管环烷酸腐蚀的措施,主要包括选用更耐蚀的316或316L材质以及改进三通结构等。
3.Effective measures are recommended to control the naphthenic acid corrosion.并提出了减少减压炉管环烷酸腐蚀的措施。

英文短句/例句

1.Naphthenic Acid Corrosion Mechanisms and anti-Corrosion Measures原油中环烷酸腐蚀机理及防腐蚀措施
2.Inhibitor of Naphthenic Acid Corrosion in Atmospheric and Vacuum Distillation Unit常减压装置环烷酸腐蚀的缓蚀剂研究
3.Experiment on the Anti-corrosion Property of Chrome Molybdenum Steel Tube in Naphthenic Acid Environment铬钼钢管耐高温环烷酸腐蚀性能试验
4.According to experiment results, measures to prevent such corrosion failure have been suggested. The main measure to control the naphthenic acid corrosion at high temperature spots is the selection of appropriate corrosion resistant materials.并结合分析结果 ,提出了控制环烷酸腐蚀主要应选择耐环烷酸腐蚀的材料等措施。
5.Liquid erosion dramatically accelerates naphtehnic acid corrosion of the stainless steels.流体冲刷明显加剧不锈钢的环烷酸腐蚀.
6.Summarization of High-temperature Naphthenic Acid Corrosion and Its Control Technique on Pipeline管线的高温环烷酸腐蚀与控制技术综述
7.Progress in Research on Mechanisms and Controlling of Naphthenic Acid Corrosion at High Temperatures高温环烷酸腐蚀机理与控制方法研究进展
8.HIGH TEMPERATURE NAPHTHENIC ACID CORROSION OF STEEL IN HIGH TAN REFINING MEDIA碳钢和不锈钢在高温环烷酸介质中的腐蚀行为
9.copper naphthenate环烷酸铜（防霉剂,防腐剂）
10.This artical briefly discusses the occurence of naphthenic acid corrosion on crude distillation unit as well as the peventive measures having been successfully taken.本文就辽河原油环烷酸的腐蚀及其采取相应的防护措施进行了简要介绍.
11.Influence of MgSO_4 Corrosive Environment on Strength of Soil Cement硫酸镁腐蚀环境对水泥土强度的影响
12.The corrosive action of acid upon an etcher's metal plate.腐蚀蚀刻器的金属盘上的酸腐蚀
13.Study on Preparation and Anticorrosion Properties of Acid-catalyzed Polysilsesquioxane Coatings;酸催化聚倍半硅氧烷涂层的制备及其耐腐蚀性的研究
14.CORROSION AND PROTECTION OF STAINLESS STEEL TANKS IN ACID MIST不锈钢储罐在酸雾环境中的腐蚀及其防护方法
15.Study on Corrosion Behavior of the Typical Metals in Rain/Acid Rain;酸雨/雨水环境中典型金属材料的腐蚀行为研究
16.Study on Corrosion Behavior of Stainless Steels in Acetic Acid Solution Containing Br Ion;含溴醋酸环境下不锈钢腐蚀行为的研究
17.Experimental Research on Stress Corrosion Cracking of X70 Pipeline Steel in Nitrate Solution硝酸盐复杂环境中X70钢的应力腐蚀试验研究
18.Experimental Investigation of Stress Corrosion Characteristics for 16MnR Steel and 15MnVR Steel in Carbonate Solution16MnR钢和15MnVR钢在碳酸盐环境中的应力腐蚀研究

相关短句/例句

acid corrosion酸腐蚀;酸性腐蚀
3)corrosion environment腐蚀环境
1.The interior corrosion environment of FGD system and its countermeasuresin Shaoguan Thermal Power Plant;韶关发电厂脱硫系统内的腐蚀环境及防腐对策
2.Analysis on corrosion environment of wind power equipment and summary on coatings protection风电装备腐蚀环境分析与涂料防护
3.The coating criterions of steel structure under different corrosion environments were particularized.对处于不同腐蚀环境中的钢结构涂装规范进行了详细说明。
4)environmental corrosion环境腐蚀
1.The design idea and system frame of SQL Server database technology in query of environmental corrosion data was elaborated.NET访问SQL Server数据库技术在环境腐蚀数据中的应用设计与实现,重点阐述SQL Server数据库技术在环境腐蚀数据中查询的设计思想和体系架构,并对其中涉及的若干关键技术进行了较为详细的介绍。
5)corrosive environment腐蚀环境
1.The effects of five single and three mixed corrosive environments on the fatigue crack growth and residual strength of aluminium alloy 2024-T3 were experimentally studied.结果表明,腐蚀环境的参与使2024-T3铝合金的疲劳裂纹扩展速率明显加快,不同腐蚀环境对疲劳裂纹扩展速率的影响程度不同,其影响的严重程度由重到轻依次为:油箱结构区、厨房与厕所、油箱积存水、盐水、潮湿空气、高空环境、干燥空气。
2.Crack length measurement technique,which used for aeronautical materials under corrosive environment,has been studied in this paper.进行了腐蚀环境下航空材料裂纹扩展的自动测量技术研究。
3.Based on the fuzzy classification of the single agent corrosive environment and its effect on the structural service reliability,this paper defined a fuzzy decision making method on design reliability of structures under multi agent corrosive environment.根据单介质腐蚀性环境的模糊分级及其对工程结构服役可靠度的影响特点 ,定义了多介质腐蚀环境下建筑结构设计可靠度的一种模糊决策方法 ,提出了腐蚀性环境下建筑结构的“设计防腐”概念及工程实施方法 ,建议针对不同腐蚀性环境应采取相应的防腐措施 ,以期取得定量意义上的防腐设计。
6)cyclic corrosion循环腐蚀
1.Two kinds of carbon fiber/epoxy composites were studied under cyclic corrosion conditions of light radiation-humidity.采用仿自然环境的氙灯光照-加湿的循环腐蚀条件对两种碳纤维/环氧树脂复合材料进行了腐蚀试验,结果表明两种材料的表面发生了严重的腐蚀,单排复合材料的力学性能发生了明显的降低,编织复合材料的力学性能变化不大,FT-IR测定表明材料表面可能发生了光化学反应。