1)crack healing裂纹愈合
1.Effect of the heating temperature and heat retaining time on the inner crack healing in steel;加热温度及保温时间对结构钢内部裂纹愈合的影响
2.One type was the dissolution of lamellar pearlite in host and the other was the formation of structure at crack healing zone.为研究钢内裂纹愈合机理,对经过热愈合处理的稀土Q235钻孔压缩试样的组织进行了光学显微镜和SEM电镜观察与分析。
3.The law of inner crack healing in 20CrMnTi steel under different heat treatment was studied.裂纹愈合区由再结晶的细小铁素体组成,并形成愈合带。
英文短句/例句
1.Study on SiC-Al_2O_3 Composite Ceramic Preparation and Its Crack-healing Properties;SiC-Al_2O_3复合陶瓷的制备及裂纹愈合研究
2.Study on the Preparation and Crack Healing of Al_2O_3/TiC Composite;Al_2O_3/TiC复合材料的制备及裂纹愈合研究
3.Study on mechanism of crack healing in Al_2O_3-MgAlON compositesAl_2O_3-MgAlON复合材料裂纹愈合机理研究
4.Study on Inner Crack Healing of Ultra-super-critical Rotor 12Cr Steel12Cr超临界转子钢裂纹愈合研究
5.Effect of heat treatment on crack-healing and strength of SiC/Al_2O_3 composites热处理工艺对SiC/Al_2O_3陶瓷裂纹愈合及强度的影响
6.Physical and Numerical Simulation of Inner Crack Healing in Metals;金属材料内裂纹愈合过程的物理模拟与计算机模拟
7.Analysis of Crack Healing in Hot Rolled Deformed Piece热轧变形轧件内部裂纹愈合实验研究和机理分析
8.Study on the Crack Self-Healing in Metals by Heat Treatment;金属材料裂纹自愈合的热处理试验研究
9.Low Temperature Sintering of Alumina Ceramics and Crack Healing Reaserch氧化铝陶瓷低温烧结与裂纹自愈合研究
10.Study on crack-healing and its effect on strength of TiC-Al_2O_3 ceramicsTiC-Al_2O_3陶瓷裂纹治愈及强度的研究
11.autogenous healing of concrete混凝土裂缝自行愈合
12.Scientists at the University of Illinois have created a synthetic material that automatically seals any tiny cracks that develop within it.伊利诺伊大学的科学家创造了一种合成材料，它能自动愈合内部的任何细微裂纹。
13.Influence of fatigue crack tip plastic zone on crack propagation behavior in TC4ELI alloyTC4ELI合金疲劳裂纹尖端塑性区对裂纹扩展的影响
14.Delayed Crack and Stress Corrosion Crack of High Strength Low Alloy Steel低合金高强钢的延迟裂纹和应力腐蚀裂纹
15.Influence of Ce on Crack Closure Effect and Intrinsic Fatigve CrackGrowth Resistance In Al-Li Alloy铈对铝锂合金裂纹闭合效应及本征疲劳裂纹扩展抗力的影响
16.Two-dimensional Stress Intensity Factors by BEM with Crack Closure Integrals边界元法结合裂纹闭合积分求二维裂纹应力强度因子
17.Research on the crack growth angles of Ⅰ-Ⅱ-Ⅲ mixed mode crack with photoelastic experimentⅠ-Ⅱ-Ⅲ复合型裂纹开裂角的光弹性试验研究
18.FRACTURE TOUGHNESS MEASUREMENT OF CAST MAGNESIUM ALLOY BY CYLINDRICAL SPECIMEN WITH RING-SHAPED CRACK用环状裂纹圆柱试样测定铸镁合金的断裂韧度
相关短句/例句
crack-healing裂纹愈合
1.Effect of heat treatment on crack-healing and strength of SiC/Al_2O_3 composites热处理工艺对SiC/Al_2O_3陶瓷裂纹愈合及强度的影响
3)healed cracks愈合裂纹
4)microcrack healing微裂纹愈合
5)inner crack healing内裂纹愈合
1.The inner crack healing process experiences two stages of closing and metallurgical bonding of crack under plastic deformation.在塑性变形条件下,内裂纹愈合过程一般经历裂纹的闭合及焊合两个阶段。
6)high temperature crack healing高温裂纹自愈合
延伸阅读
淬火裂纹和非淬火裂纹的特征及实例分析淬火裂纹是指在淬火过程中或在淬火后的室温放置过程中产生的裂纹。后者又叫时效裂纹。造成淬火开裂的原因很多，在分析淬火裂纹时，应根据裂纹特征加以区分。 一、淬火裂纹的特征 在淬火过程中，当淬火产生的巨大应力大于材料本身的强度时，便会导致裂纹产生。淬火裂纹往往是在马氏体转变开始进行后不久产生的，裂纹的分布则没有一定的规律，但一般容易在工件的棱角槽口、截面突变处形成。 在显微镜下观察到的淬火开裂，可能是沿晶开裂，也可能是穿晶开裂；有的呈放射状，也有的呈单独线条状或呈网状。 因在马氏体转变区的冷却过快而引起的淬火裂纹，往往是穿晶分布，而且裂纹较直，周围没有分枝的小裂纹。 因淬火加热温度过高而引起的淬火裂纹，都是沿晶分布，裂纹尾端尖细，并呈现过热特征：结构钢中可观察到粗针状马氏体；工具钢中可观察到共晶或角状碳化物。 表面脱碳的高碳钢工件，淬火后容易形成网状裂纹。这是因为，表面脱碳层在淬火冷却时的体积胀大比未脱碳的心部小，表面材料受心部膨胀的作用而被拉裂呈网状。 二、非淬火裂纹的特征 淬火后发生的裂纹，不一定都是淬火所造成的，一般可根据下面的特征来区分。 淬火后发现的裂纹，如果裂纹两侧有氧化脱碳现象，则可以肯定裂纹在淬火之前就已经存在。淬火冷却过程中，只有当马氏体转变量达到一定数量时，裂纹才有可能形成。与此相对应的温度，大约在250℃以下。在这样的低温下，即使产生了裂纹，裂纹两侧也不会发生脱碳和出现明显氧化。所以，有氧化脱碳现象的裂纹是非淬火裂纹。 如果裂纹在淬火前已经存在，又不与表面相通，这样的内部裂纹虽不会产生氧化脱碳，但裂纹的线条显得柔软，尾端圆秃，也容易与淬火裂纹的线条刚健有力，尾端尖细的特征区别开来。 三、实例分析 实例一： 40Cr钢制成的转子轴，经锻造、淬火后发现裂纹。裂纹两侧有氧化迹象，经金相检验，裂纹两侧存在脱碳层，而且裂纹两侧的铁素体呈较大的柱状晶粒，其晶界与裂纹大致垂直。结论：裂纹是在锻造时形成的非淬火裂纹。 当工件在锻造过程中形成裂纹时，淬火加热即引起裂纹两侧氧化脱碳。随着脱碳过程的进行，裂纹两侧的碳含量降低，铁索体晶粒开始生核。当沿裂纹两侧生核的铁素体晶粒长大到彼此接触后，便向离裂纹两侧较远的基体方向生长。由于裂纹两侧在脱碳过程中碳浓度的下降，也是由裂纹的开口部位向内部发展，因而为铁素体晶粒的不断长大提供了条件，故最终长大为晶界与裂纹相垂直的柱状晶体。