1)enfold-defect折叠缺陷
1.The cause of extrusion enfold-defect at the top of piston is analyzed,which is because of the thin remainder.对活塞顶部挤压折叠缺陷产生的原因进行了分析,发现折叠缺陷是由于余料太薄引起的缩尾性折叠;分别对增厚坯料法、方形坯料法和两步挤压法进行了分析比较,结果表明采用增加坯料厚度的方法来防止折叠不仅增加了材料的浪费,也会增大后续的机加工量,是不经济的;方形坯料虽说可以有效的避免活塞顶部金属对流情况,但是会在活塞环岸内侧产生折叠;而两步挤压法有效的防止了活塞销顶部金属对流的情况,有效的避免了活塞顶表面折叠的产生。
英文短句/例句
1.Experimental Analysis on Outer Folder on GCr15 Steel TubeGCr15钢管外折叠缺陷成因的检测研究
2.Analysis of Folding Defect of GH3600 Tube Inner WallGH3600精细薄壁管内壁折叠缺陷分析
3.Reasons and Solutions About Folding Defect in Extrusion Forming of Thrust Bearing止推轴承座挤压成形过程中产生折叠缺陷的原因及解决方案
4.CLINICAL APPLICATION OF THE NASOLABIAL FOLD WRAPPED FLAP ON REPAIRING PINNA NASI DEFECT应用鼻唇沟折叠皮瓣修复鼻翼缺损
5.Defect Modes Based on Negative Refractive Index Structural Defects Coupled in One-dimensional Photonic Crystals;一维光子晶体中多负折射率缺陷导致的缺陷模
6.Defect mode in positive-negative index photonic crystal with negative refractive index structural defect含负折射率缺陷的正负交替光子晶体的缺陷模
7.folding intermediate折叠中间体，折叠中间态
8.capable of collapsing or being collapsed.能够折叠或者被折叠。
9.Gatefold: Also called Fold-out, Thrown-out.对门折（折叠插页）
10.THEORY AND APPLICATION OF PRESTACK MIGRATION IN FLAW DETECTION OF CONCRETE STRUCTURE混凝土结构缺陷检测中的叠前偏移理论及应用
11.Thought of system defects from an analysis of recognition dilemma---system defects of the new-type rural Cooperative Medical Service and the countermeasures;认同尴尬折射制度缺陷——漫谈新型农村合作医疗的制度缺陷及对策
12.Economic Ordering Quantity Models for Items with Fuzzy Imperfect Rate and Price Discount;含价格折扣和模糊缺陷率的EOQ模型研究
13.The Growth of Double Refraction Crystal YVO_4 by Czochralski Methodand and Study the Growth Defects提拉法生长双折射晶体钒酸钇（YVO_4）及其缺陷研究
14.The Research of Fabricating Two-Dimensional Photorefractive Photonic Lattice within Linear-defect具有线缺陷二维光折变光子晶格的制备研究
15.Impurity Band in One-dimensional Photonic Crystal Containing Defect Layers with Negative Refractive Index含负折射率缺陷的一维光子晶体的杂质带
16.Defects due to an unsatisfactory rate of teeming. This kind defects include splashing, rippled surface, and laps or folds.由于浇注速度掌握不好而引起的缺陷。这种缺陷包括飞溅、波皱面以及重皮或摺叠。
17.concertina movement折叠［蛇腹］式构造
18.automatic layboy(桨板)自动折叠机
相关短句/例句
defective protein folding and trafficking蛋白折叠运输缺陷
3)lap blisters折叠气泡(玻璃缺陷)
4)stacking fault叠层缺陷
5)break marks横折缺陷
1.The break marks is a kind of strip marks that is vertical to rolling direction, occurring at some locations of hot-rolled steel strip during uncoiling.热轧低碳钢卷开卷后出现横折缺陷是一种常见现象,无论是国内产品还是进口产品都不同程度地出现横折缺陷,给用户带来许多不便和损失。
2.Based on spike height resulting in break marks,the new technique of eliminating break marks by getting microstructure of quasi-acicular ferrite in hot strip mill was applied.根据上下屈服点应力差是产生横折的根本原因,采用"控制显微组织形态,降低上下屈服点应力差"来消除热轧带钢横折缺陷。
6)inner fold defects内折缺陷
1.The influence of over-heat and draw speed on inner fold defects of seamless steel tube is analyzed in hot test process of 20 steel from point of view of inner solidified organization of CC billet.从连铸坯内部凝固组织的角度出发,分析了20钢在热试过程中,过热度、拉速对无缝管内折缺陷的影响,并提出了改善内部组织的措施,以减少内折废品的产生。
延伸阅读
折叠折叠overlap zhedje 折必(o verlaP)钢材表面缺陷之一，表现为 表面层金属的折合分层。外形与裂纹相似，其缝隙与表 面倾斜一定角度，常呈直线形(见图)，也有的呈曲线 型或锯齿形。折叠的分布有明显的规律性，一般是通长 地、也有的是局部或断续地分布在产品表面上。折叠内 有较多的氧化铁皮。双层金属折合面有脱碳层，在与金\…蘸蘸 折叠 属本体相接触一侧的折合缝壁上，尤为严重。钢管内表 面和外表面产生的折叠分别称内折叠和外折叠。产品 表面上一般不允许有折叠。折叠产生的原因是:(l)轧 制时因轧件出耳子并在以后被轧折。压下女分配不当， 导板安装不正、不牢、轧辊窜动、立辊挤压过大或局部 压下过大等都能使轧件出耳子;(2)半成品轧件严重的 剑伤被轧折;(3)上下万L型尺寸不吻合轧件出棱子被轧 折;(4)钢坯有耳子或钢坯表面清理沟痕过陡，深宽比 不够，在以后被轧折;(5)钢板轧制中形成了大波浪并 被轧折;(6)因轧辊棍面剥落或刻痕过深轧出的凸包以 后被折合回去;(7)钢管的内折叠主要是由料札穿孔时 产生孔腔或内裂纹所致(见针札穿孔原理)。自动札管 机轧管时易产生深的内直道，到冷加工时则成为直线 形内折叠;外折叠多由于管坯表面有夹杂，轧制时出耳 子或表面上有裂纹和深的刮伤经压缩所致。 防止和消除折叠的办法有:(1)严格检查坯料质 量，耳子高度或清理沟痕不合格的坯料不投产，(2)札 糟刻痕不合格的轧辊不得使用;(3)完善孔型设计，加 强轧机调整，正确安装轧辊和导卫装里，防止轧件出耳 子和产生梭子;(4)及时更换磨损严重的轧槽、导卫装 置和辊面剥落的轧辊，以保证轧件尺寸和表面质量符 合规定;(5)钢板生产中合理配置辊型(见棍型设计)， 加强轧机调整，防止产生大波浪。 (刘贤才李连诗)