1)retained austenite残留奥氏体
1.Effect of Retained Austenite in Impact Wear;冲击磨损条件下残留奥氏体的作用
2.It is shown that the microstructure of Q&P steel is lath martensite and retained austenite(8%~15%).采用扫描和透射电镜进行了组织观察与分析,发现其组织主要由板条马氏体和8%~15%的残留奥氏体组成,残留奥氏体呈膜状。
3.The results show that polygonal ferrite,granular bainite and larger amount of stabilized retained austenite can be obtained after hot rolling.结果表明,热轧后能够获得多边形铁素体、粒状贝氏体和大量稳定的残留奥氏体组织。
英文短句/例句
1.Review on the Relation between Heat Treatment and Retained Austenite Formation of Cold Rolled TRIP-aided Steels冷轧TRIP钢的热处理与残留奥氏体形成的关系
2.Through the processing, it becomes a kind of extremely hard, wear-resistant and dispersed ledeburite structure which consists of martensite, retained austenite and carbide phases.表面层极硬、耐磨而弥散的莱氏体是由马氏体+残留奥氏体+碳化物相组成。
3.Study on the Content of Retained Austenite ADI奥－贝球铁中残余奥氏体含量的研究
4.Rietveld Full Pattern Fitting Method for Quantitative Phase Analysis of Austenite in Iron and SteelRietveld精修定量分析钢中残余奥氏体
5.Microstructure and Stability of Retained Austenite in a High Al-Containing TRIP Steel高铝TRIP钢的微观组织与残余奥氏体稳定性研究
6.Relation between Processing and Retained Austenite Formation of Hot Rolled TRIP-aided Steels热轧TRIP钢的加工工艺与残余奥氏体形成的关系
7.Transformation behavior of retained austenite in TRIP steel under stress-strainTRIP钢中残余奥氏体相变与断裂机制研究
8.Retained austenite in steel--Quantitative determination--Method of X-ray diffractometerGB/T8362-1987钢中残余奥氏体定量测定X射线衍射仪法
9.Influence of the Tempering Technology on Retained Austenite and Hardness of High-Speed Steel Rolls回火工艺对高速钢轧辊残余奥氏体和硬度的影响
10.Pharmacokinetics and Residue Elimination of Oxytetracycline in Hybrid Tilapia, Oreochromis Aureus×O. Niloticus;土霉素在奥尼罗非鱼体内的药动学及残留消除规律研究
11.Studies on Pharmacokinetic and Tissue Residues of Orbifloxacin in Rabbits奥比沙星在兔体内的药物动力学与残留消除规律研究
12.ferritic-austenitic alloy steel铁素体奥氏体合金钢
13.Process Research on the Isothermal Quenching of Ductile Iron of Austenite and Bainite;奥氏体贝氏体球铁等温淬火工艺研究
14.Krupp austenitic steel克虏伯奥氏体不锈钢
15.austenite grainsize determination奥氏体晶粒大小测定法
16.Boronizing of ZG1Cr18Ni9 austenite stainless steelZG1Cr18Ni9奥氏体不锈钢的渗硼
17.Influences of Beijing para-Olympics on Chinese sports for disabled;北京残奥会对中国残疾人体育的影响
18.THE EFFECT OF PRIOR AUSTENITIC GRAIN BOUNDARIES ON NUCLEATION OF(225)_γ MARTENSITE IN STEELS钢中原始奥氏体晶界对(225)_γ马氏体形核的影响
相关短句/例句
residual austenite残留奥氏体
1.The results show that the microstructure obviously varies with the change of depth in laser hardened zone;the large amount of residual austenite is produc ed due to existence of ally elements in the steel during laser transformation ha rdening,which decrease surface hardness;with the scanning spee.结果表明 ,18Cr2Ni4W钢在复合工艺作用下 ,随着表面硬化区层深的变化 ,其组织结构发生明显变化 ;由于钢中存在大量的合金元素 ,致使表面硬化层产生大量的残留奥氏体 ,降低了表面的硬度 ;随着激光扫描速度的增加 ,硬化区硬度增大。
2.The hardness and microstructure were examined and the amounts of residual austenite (A R) in the steel were determined by XRD.X射线衍射分析发现 ,低温回火后的W 6Mo5Cr4V2高速钢中含有较多残留奥氏体 (约 15 8% ) ,它们在一定程度上可提高钢的韧性 ,阻碍冲击载荷下裂纹的形核与扩展。
3)retained austenite残留奥氏体;残余奥氏体
4)transformation of retained austenite残留奥氏体转变
1.Several questions on high speed steels which are still considered unsolved, such as ‘balanced carbon’,secondary hardening, transformation of retained austenite, and fish scale fracture have been reviewed briefly.对高速钢中合金元素与碳的关系、二次硬化、残留奥氏体转变、萘状断口等几个据认为尚无最后结论的研究课题 ,进行了简要的回顾。
5)retained austenite残留［余］奥氏体
6)stability of retained austenite残留奥氏体稳定性