氧化铝模板,alumina template英语短句,例句大全

氧化铝模板,alumina template
1)alumina template氧化铝模板
1.Effect of heat treatment process on photoluminescence of anodic alumina template;处理温度对阳极氧化铝模板光致发光性能的影响
2.The influence of parameters on the pore size of the alumina template;阳极氧化工艺对氧化铝模板孔径的影响
3.The absorption border shift to the infrared direction in contrast to the anodic alumina template is due to the increasing of dispersion center.紫外-可见光吸收光谱测试表明:Cu/Al2O3组装体吸收光谱上仅呈现出一个吸收带边,无等离子共振吸收峰,且吸收边相对于阳极氧化铝模板发生了红移。

英文短句/例句

1.The barrier-layer alumina films and porous-layer alumina make up of nanometer alumina membrane.其中阻挡层氧化铝和多孔层氧化铝构成纳米氧化铝模板。
2.Preparation of patterned anodic aluminum oxide template by constant current density process恒流法制备图案化的阳极氧化铝模板
3.The Preparation of Anodic Aluminum Oxide Template and Nanowires Template Synthesis;多孔氧化铝模板的制备及模板法合成镍纳米线
4.Synthesis of One-Dimensional Functional Nanomaterials Using Alumina Membrane as Template;氧化铝模板法制备一维功能纳米材料
5.Synthesis of One-dimensional Inorganic Nanomaterials Using Alumina Membrane as Template;氧化铝模板法制备一维无机纳米材料
6.Preparation Technology of Porous Anodic Aluminum Oxide Template多孔阳极氧化铝模板制备工艺的研究
7.Preparation of Titanium Dioxide Nanotube on Anodizing Aluminum Oxide Template;基于阳极氧化铝模板的二氧化钛纳米管制备
8.Fabrication of Cerium-doped Titanium Dioxide Nanotubes by Using Anodized Aluminum Oxide Template氧化铝模板法制备Ce掺杂二氧化钛纳米管
9.Preparation of Shape-controllable Metal Nanowires Based on AAO Template-method;基于氧化铝模板法制备形状可控的金属纳米线
10.The Fabrication of One-dimensional Nanostructure Based on the AAO Template;基于氧化铝模板的一维纳米结构的构筑与表征
11.Fabrication and Photoluminescence Properties of Porous Anodic Alumina Templates;多孔氧化铝模板的制备及其光致发光性能
12.Preparation of Porous Alumina Template and Assembly of Nano-Channel Array System;多孔氧化铝模板制备与纳米阵列体系组装
13.The Study on Luminescence of ZnO Nano-particles Loaded into Porous Alumina Hosts;纳米ZnO在多孔氧化铝模板内的发光特性的研究
14.Synthesis of One-Dimensional Metal Nanomaterials by AAO Template-Assisted Electrodeposition;氧化铝模板法电沉积制备一维金属纳米材料
15.Fbrication of Single-crystal Magnetic Nanowire Arrays Using AAO Template;氧化铝模板法制备单晶磁性纳米线阵列研究
16.Application of Nano-sized Materials Fabricated by Porous Anodic Alumina Template;氧化铝模板组装纳米材料及其应用研究
17.Preparation of Anodic Porous Alumina Template with Highly Ordered Array Structure;具有规则阵列结构的阳极氧化铝模板的制备
18.Electrochemical deposition of Co nanowire arrays in porous alumina membrane by alternating current method多孔氧化铝模板中交流沉积钴纳米线阵列

相关短句/例句

AAO template氧化铝模板
1.In this work, potential_modulation method was used in two_step anodization process to make an AAO template with Y_type nanochannels.　利用两步氧化法,通过对氧化直流电压进行周期性调制可制备出带有Y型孔道的氧化铝模板;然后以金属钴为催化剂,乙炔为碳源,通过CVD法制取得到具有规则Y型分支的碳纳米管阵列。
2.The AAO template with nano-channels was synthesized and filled with transient metal-oxide NiO by sol-gel method, and their electrochemical properties were primarily studied.制备具有双通纳米孔道填充过渡金属氧化物NiO的氧化铝模板,初步表征其电化学性质。
3.Magnetic oxide iron nanowires are obtained by removing AAO template.通过溶胶-凝胶法在氧化铝模板(AAO)中制备出了磁性Fe_2O_3纳米线阵列,然后去除AAO模板得到磁性Fe_2O_3纳米线。
3)anodic aluminum oxide template氧化铝模板
1.Synthesis of La nano wires by anodic aluminum oxide template in ionic liquids;在离子液体中用阳极氧化铝模板电沉积制备稀土镧纳米线
2.Pd-Ni and Pd-Ag alloy nanowires arrays have been fabricated in the nanopores of anodic aluminum oxide template with 200 nm in diameter and 60 μm in depth by galvanostatic electrodeposition.在孔深60μm直径200 nm的通孔氧化铝模板中,采用恒电流沉积法制备了钯镍与钯银合金纳米线阵列。
4)anodic alumina membrane氧化铝模板
1.Preparation and characterization of nickel nanowires by direct electrodeposition in anodic alumina membrane;基于氧化铝模板直接电沉积法镍纳米线的制备与表征
2.Highly ordered zinc oxide nanowire/tube arrays were prepared by a sol-gel method in the pores of anodic alumina membranes (AAM).用溶胶-凝胶法在氧化铝模板中制备了直径约为15、30、50、60nm的有序氧化锌纳米线/管阵列。
3.Bi/Sb and Ag/Bi/Ag segmented nanowire heterojuction arrays were fabricated by the step pulsed electrodeposition in anodic alumina membranes and characterized by FESEM, XRD and TEM.采用分步脉冲电沉积技术,在氧化铝模板中制备了Sb/Bi和Ag/Bi/Ag纳米线异质结阵列,对其进行了结构表征,研究了这些纳米线异质结阵列的电输运特性。
5)aluminium oxide template氧化铝模板
6)aluminum oxide template氧化铝模板
1.Ordered porous anodic aluminum oxide templates were prepared by a two-step anodization approach where sulfuric acid solution was employed as an electrolyte.以硫酸溶液为电解液,采用二次阳极氧化工艺制备高度有序的多孔阳极氧化铝模板。
2.In this paper,porous aluminum oxide template with ordered nanoarray is introduced,and because of quatization it has many special properties like electrical,magnetic,optical,etc.由多孔阳极氧化铝模板制备有序纳米阵列因量子化具有各种特殊性能,准一维的电子输运环境使其磁阻随磁场变化有极值出现,表面缺陷的增加使其光致发光增强,纳米线阵列对各个方向透过光的损耗不通而具有偏振性,磁性能方面具有强烈的各向异性等。